Binder-Free Laser Induced Graphene-Mno2 Composite Electrodes For High Areal Energy Density Flexible Supercapacitors

Ankitha Rao,Somashekara Bhat,Shounak De

DOI: https://doi.org/10.1016/j.electacta.2024.144152

IF: 6.6

2024-03-28

Electrochimica Acta

Abstract:The synthesis of Laser-Induced Graphene (LIG) through the laser ablation process of carbon-containing materials is a rapid and scalable process which enables the production of graphene in a cost-effective manner. In recent years, metal oxide – graphene composite electrodes have gained a lot of importance due to their use in various Energy Storage Devices (ESDs). In our investigation, we manufacture composite electrodes of manganese dioxide (MnO 2 ) and LIG through a hydrothermal process and use it as electrodes in Flexible Supercapacitors. This method deviates from traditional procedures as it eliminates the requirement for binders in creating composite electrodes, given that MnO 2 can be directly deposited onto the LIG electrodes. The assembled all-Flexible Supercapacitor (FSC), featuring unique LIG-MnO 2 composite electrodes, showcased a remarkable areal capacitance of 66.5 mF cm −2 at 5 mV s −1 scan rate. The device also exhibited a very high areal energy density (2.3 mWh cm −2 ) and power density (19.7 mW cm −2 ) at 0.2 mA cm −2 current density. Also, 82% capacitance retention was observed at the end of 2000 cycles and the device also exhibited a good flexibility during bending tests, as evidenced by an 80% capacitance retention after 100 bending cycles.

electrochemistry