Importance of Lithium Coordination Structure to Lithium-Ion Transport in Polyether Electrolytes with Cyanoethoxy Side Chains: An Experimental and Theoretical Approach
Riho Matsuoka,Masayuki Shibata,Kousuke Matsuo,Ryansu Sai,Hiromori Tsutsumi,Kenta Fujii,Yu Katayama
DOI: https://doi.org/10.1021/acs.macromol.0c01634
IF: 5.5
2020-10-16
Macromolecules
Abstract:Polymer electrolytes (PEs) have been studied as an alternative to the current liquid electrolytes in lithium-ion batteries. Although polyether electrolytes have been developed for more than decades, these electrolytes have limitations such as low ionic conductivity and a small lithium-ion (<i>t</i><sub>Li<sup>+</sup></sub>) transference number. In this work, we combine spectro(electro)chemical analyses with molecular dynamics (MD) simulations to understand the complex interaction within the electrolyte, consisting of a polyether having both ether and cyano groups (poly(3-(2-cyanoethoxymethyl)-3-ethyloxetane), PCEO) mixed with various concentrations of lithium bis(trifluoromethanesulfonyl)imide (LiTFSI), to clarify the Li<sup>+</sup> coordination structure as well as its relevance to Li<sup>+</sup> conductivity. Applicability of MD simulations was validated by high-energy X-ray total scattering measurements. The local coordination structures around Li<sup>+</sup> were successfully estimated by the distribution function obtained from MD simulations, which suggested the preferable coordination of the cyano group with Li<sup>+</sup> over the other elements, including ether oxygen. Further support came from infrared (IR) spectroscopy, where the estimated coordination number (<i>N</i>) obtained from the IR peak area of the deconvoluted CN stretching vibration (<i>ca</i>. 2250–2280 cm<sup>–1</sup>) agreed well with the MD result. Arrhenius plots of the ionic conductivity showed a curved shape, indicating that the segmental motion of the polymer main chain was responsible for Li<sup>+</sup> transportation in PCEO electrolytes. The Li<sup>+</sup> conductivity varied with the salt concentration and was sensitive to the Li<sup>+</sup> coordination structure. The highest Li<sup>+</sup> conductivity was achieved at an intermediate salt concentration, where Li<sup>+</sup> coordinated mostly by the cyano group (<i>N</i> = 2.2), followed by the TFSI anion (<i>N</i> = 1.3), and only a small contribution was from ether oxygen (<i>N</i> = 0.5). The characteristic cocontribution of a cyano group and ether oxygen to the Li<sup>+</sup> coordination structure can be responsible for the improved Li<sup>+</sup> conduction, by accelerating the interchain Li<sup>+</sup> transfer, involving a decoordination process, (short-range Li<sup>+</sup> conduction) while maintaining good segmental mobility of the polymer (long-range Li<sup>+</sup> conduction). The results emphasize the importance of the coordination structure to the electrolyte property, which can provide additional knobs to improve the ionic conductivity as well as the Li<sup>+</sup> transference number, leading to further improvements in the performance of polymer electrolytes.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.macromol.0c01634?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.macromol.0c01634</a>.Details of the monomer and polymer synthesis; <sup>1</sup>H and <sup>13</sup>C NMR spectra of the monomer and polymer; experimental procedures for the HEXTS measurement; descriptor used for MD simulations; partial charge values of PCEO and LiTFSI; TG curves for pure PCEO and PCEO electrolytes; TG–MS curves for pure LiTFSI; <i>S</i>(<i>q</i>) and <i>r</i><sup>2</sup> [<i>G</i>(<i>r</i>) – 1] for PCEO<sub>3</sub>LiTFSI obtained from HEXTS measurements and MD simulations; partial <i>G</i><sup>MD</sup>(<i>r</i>)s for PCEO electrolytes; details of the IR peak analysis, molar IR absorption coefficient analysis, and additional atom–atom pair correlation functions; ATR–FTIR spectra of PCEO<sub><i>a</i></sub>LiI electrolytes and PCEO<sub><i>a</i></sub>LiTFSI electrolytes (<i>a</i> = 1, 3, and 10); frequency dependence of imaginary impedance (<i>Z</i>″) for PCEO<sub><i>a</i></sub>LiTFSI (<i>a</i> = 1, 3, and 10); and time dependence of DC polarization, Nyquist plots, and measured parameters for the <i>t</i><sub>Li<sup>+</sup></sub> calculation for PCEO<sub><i>a</i></sub>LiTFSI (<i>a</i> = 1, 3, and 10) and PBuEO<sub>3</sub>LiTFSI (<a class="ext-link" href="/doi/suppl/10.1021/acs.macromol.0c01634/suppl_file/ma0c01634_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
polymer science