Abstract:<p>Biofouling and cavitation erosion are the key important factors causing the degradation and fatigue failure of metal materials in seawater. Herein, a series of polyurethane (PU) /ZIF-8 (PHZ) composite coatings were successfully synthesized with different sizes of ZIF-8 nanoparticles (NPs) for antifouling property combined with cavitation erosion resistance. The morphology and structure of the PHZ composite coatings were characterized by XRD, ATR-FTIR, SEM and AFM. The static water contact angle, dynamic mechanical analysis and thermo gravimetric tests further confirmed that the ZIF-8 NPs could improve the hydrophobic, mechanical and thermal properties of the PU coatings. Importantly, the effect of the ZIF-8 NPs with different sizes on the performance of the PHZ coatings was also investigated. The PHZ1 coating with the ZIF-8 NPs (~50 nm) displayed the highest static water contact angle (105°), the largest tensile strength (6.78 MPa) and the best thermal stability among these PHZ coatings. The antifouling properties of the PHZ coatings were also tested against marine diatom (<em>Nitzschia closterium</em>). Especially, the biofouling attachment rate of the PHZ1 coating was 0.51%, which was far less than that of pure PU coating (92%). Moreover, the mass loss of the PHZ1 coating was only 8.9 mg after cavitation test for 24 h. Notably, both antifouling and anti-cavitation properties of the PHZ coatings were inversely proportional to the particle size of the ZIF-8 NPs. The present study offers a simple and green coating technology that combines the antifouling and anti-cavitation to promote the development of ZIF/PU nanocomposite systems for practical applications.</p>

Enhanced anti-biofouling ability of polyurethane anti-cavitation coating with ZIF-8: A comparative study of various sizes of ZIF-8 on coating