Facile Microwave Synthesis of a Narrow-Band Green-Emitting Phosphor Cs 3 MnBr 5 and the Effect of Anion Substitution on Its Luminescence Properties

Yingfang Tao,Haixing Zhao,Yan Xu,Deyin Wang,Yuhua Wang

DOI: https://doi.org/10.1021/acs.inorgchem.2c00717

IF: 4.6

2022-05-26

Inorganic Chemistry

Abstract:A bright blue light excitable and narrow-band green-emitting phosphor Cs₃MnBr₅ has been synthesized by a facile microwave radiation method within 2 min. The influence of the matrix on its steady-state and transient-state luminescence properties is investigated by partial substitution of Br^- ions by Cl^- ions. The incorporation of Cl^- ions in Cs₃Mn(Br_1-<i>x</i>Cl_<i>x</i>)₅ resulted in almost no change in the emission maxima of Mn²⁺, which is attributed to the synergistic effect of reduced covalency and increased crystal field strength caused by the replacement of Br^- ions by Cl^- ions. Meanwhile, the emission of Mn²⁺ decreases with the increasing Cl^- content, which is caused by different thermal quenching of Mn²⁺ emission in the mixed Cl^-/Br^- coordination. Moreover, the incorporation of Cl^- in Cs₃Mn(Br_1-<i>x</i>Cl_<i>x</i>)₅ was found to have different effects on the lifetime of Mn²⁺ at different temperatures, that is, at room temperature, the lifetime of Mn²⁺ decreases with the increasing Cl^- content, while at liquid nitrogen temperature, the lifetime of Mn²⁺ increases upon increasing the Cl^- content. The former is due to the different thermal quenching for different coordinations of Mn²⁺ with Cl^- and Br^-, while the latter is due to the weaker spin-orbit coupling of the Mn²⁺ ion caused by the interaction with the lighter Cl^- ions, which makes the spin selection rule stricter and leads to a longer lifetime of Mn²⁺ consequently.

chemistry, inorganic & nuclear