Abstract:After primary refining, liquid steel presents elevated total oxygen (T.O.) values due to the oxidizing characteristic of this stage during steel production.1–3) The liquid steel is submitted to deoxidation process during the tapping process in order to decrease total oxygen content. At this moment, numerous inclusions are formed in liquid steel as the result of reactions between dissolved oxygen and metallic alloys added as deoxidizer.4,5) These inclusions must be removed to obtain a higher level of steel cleanliness, with this process being one of the main functions of secondary refining slags.6,7) The removal of inclusions occurs in three steps: flotation, separation, and dissolution.7–10) Moreover, slag liquid fraction is considered the portion that effectively reacts with inclusions, leading to their dissolution from liquid steel.9–12) In most cases, only ladle metallurgy is not Evaluation of Thermodynamic Driving Force and Effective Viscosity of Secondary Steelmaking Slags on the Dissolution of Al2O3-Based Inclusions from Liquid Steel