Graphene/polyaniline waterborne composite coatings for metallic bipolar plates

Yiquan Qi,Jincan Cui,Fucheng Guo,Jing Li

DOI: https://doi.org/10.1016/j.porgcoat.2024.108829

IF: 6.6

2024-10-04

Progress in Organic Coatings

Abstract:Waterborne composite coatings were formulated for protection of metallic bipolar plates. The challenges lied in two aspects, one was the confliction between high electrical conductivity and good corrosion protection properties; the other was the water dispersibility of the constituent phases. Water-solubility of polyaniline (PANI) were controlled by adding polystyrene sulfonic acid during the polymerization of aniline. Graphene was functionalized by p-aminobenzoic acid and p -phenylenediamine to enhance the compatibility with PANI, while keeping the electrical conductivity of graphene at around 169 S/cm. Upon in-situ polymerization of the functionalized graphene/PANI composites, the electrical conductivity varied significantly from 41 S/cm to 91 S/cm with the surface functionality of graphene. The composite coatings were prepared thereafter with functionalized graphene/PANI/carbon black on the surface of 316 L stainless steel by centrifugal spraying coating. The interfacial contact resistance of the coatings reached 4 mΩ·cm 2 , comparable to Au coatings, but the corrosion current density was 4.37 μA/cm 2 due to the existence of the hydrophilic groups in waterborne coatings, like amino groups and sulfonic acid groups. A post-treatment was carried out to consume some of the amino groups, so that the corrosion current density was decreased to 0.88 μA/cm 2 .

materials science, coatings & films,chemistry, applied