Preparation of phytic acid‐based green intumescent flame retardant and its application in PLA nonwovens

Yufan Yang,Xingguo Wang,Bin Fei,Hongfei Li,Xiaoyu Gu,Jun Sun,Sheng Zhang
DOI: https://doi.org/10.1002/pat.5316
IF: 3.348
2021-04-11
Polymers for Advanced Technologies
Abstract:<p>As a bio‐based and biodegradable textile, poly (lactic acid) (PLA) nonwovens are an important supplement for nature cotton, flax, and silk. This work concentrated on improving the flame retardancy of PLA nonwovens by introducing a novel eco‐friendly flame retardant (TPA), which was synthesized from phytic acid and tris(hydroxymethyl)methyl aminomethane. The structure, composition, and properties of TPA were fully characterized, and the results showed that TPA owned excellent thermal expansion performance. The flame retardancy of PLA nonwovens was efficiently improved by the presence of TPA. For PLA/23%TPA sample, the molten droplet was inhibited and the damaged area was decreased by 71.8%. The LOI value was increased from 18.0% of control PLA to 26.5%, and the peak heat release rate (pHRR) and total heat release rate (THR) were decreased by 30.2% and 29.0%, respectively. Besides, TG analysis confirmed a great char‐forming capability of the treated fabrics with the residue amount increasing from 1.8 to 11.6 wt% at 800°C. TPA released vapor, phosphorus radicals into the gas phase, and also promoted to form a compact char barrier in the condensed phase, which enhanced the carbonization and flame retardancy of PLA nonwovens. To our best knowledge, our work is one of the few studies focused on the flame retardancy of bio‐based PLA nonwovens.</p>
polymer science
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to improve the flame - retardant performance of polylactic acid (PLA) non - woven fabrics. Polylactic acid is a bio - based and degradable textile material. As an important supplement to natural cotton, flax and silk, it has the advantages of high strength, good drapability, good touch and wrinkle resistance. However, PLA non - woven fabrics are flammable during combustion and are accompanied by severe dripping phenomena, which greatly limit their applications. Therefore, researchers have developed a new type of environmentally friendly intumescent flame retardant (TPA), and by combining TPA with PLA non - woven fabrics, its flame - retardant performance has been significantly improved. Specifically, TPA is synthesized by phytic acid (PA) and tris(hydroxymethyl)aminomethane (Tris) through an acid - base reaction. The introduction of TPA not only effectively inhibits the dripping phenomenon of PLA non - woven fabrics, reduces the damaged area, but also significantly increases the limiting oxygen index (LOI) of the material, reduces the peak heat release rate (pHRR) and the total heat release (THR). In addition, thermogravimetric analysis (TGA) has confirmed that the treated fabric forms a large amount of char layer, and the residual amount has increased from 1.8% to 11.6%, indicating that TPA promotes the carbonization process of PLA non - woven fabrics at high temperatures, thereby enhancing their flame - retardant performance.