Gold nanohexagrams via active surface growth under sole CTAB control

An Su,Qian Wang,Liping Huang,Yonglong Zheng,Yawen Wang,Hongyu Chen

DOI: https://doi.org/10.1039/d3nr03006g

IF: 6.7

2023-08-30

Nanoscale

Abstract:The synthesis of homochiral nanostructures involves not only the chiral ligand, but also CTAB. The latter is often treated as a weak ligand unable to compete with the thiol-based chiral ligand. Here, we show that CTAB alone is able to induce Active Surface Growth on Au nanoplates, giving curved tips and steep ridges in the resulting nano-hexagrams. The growth materials (Au 0 ) are diverted to a few active sites, whereas the rest of the Au surfaces are inhibited. Modulation of the growth rate by the ratio of ascorbic acid to Au precursor gives a continuous change of the growth modes, explaining the main trends of shape evolution and the inequivalent growth of the equivalent surfaces. With only CTAB as the ligand, the fact that ridges and spikes could be formed in defiance of facet control suggests that the role of CTAB cannot be ignored in the chiral synthesis and that the precise modulation of the Active Surface Growth could be the key to rational synthetic controls.

materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology,chemistry

What problem does this paper attempt to address?

This paper mainly investigates how to induce the formation of gold nanostructures with specific shape features, especially nano-hexagons with spine-like structures, only through the use of cetyltrimethylammonium bromide (CTAB) without chiral ligands. The study found that CTAB can trigger Active Surface Growth (ASG) even without thiolate ligands traditionally used for chiral synthesis, resulting in the formation of curved tips and steep spines at the edges of gold nanosheets. These spine-like structures resemble those in chiral structures, but no chiral inducer was used in this experiment.

The authors controlled the growth rate by adjusting the ratio of ascorbic acid (AA) as the reducing agent to the gold precursor, and found that this can continuously change the growth mode and explain the main trend of shape evolution and uneven growth of the equivalent surface. The formation of spine-like structures under the condition of only CTAB as the ligand indicates the crucial role of CTAB in chiral synthesis, and precise control of ASG may be the key to achieving rational synthesis control.

In addition, the study also showed that CTAB can influence the vertical growth of nanostructures, forming high curvature tips and spines, which is different from the conventional explanation based on stable crystal facets or minimum surface energy. By dynamically controlling the growth conditions, the study reveals the important role of CTAB in the growth of gold nanostructures, providing a new perspective for understanding chiral induction.