Abstract:Manganese (Mn) oxide possessing considerable catalytic activity toward oxygen reduction reaction (ORR) exhibits promising potential in driving energy conversion technologies. However, small specific surface area, poor electron conductivity, and more importantly uncontrollable microgeometry of crystal greatly restraint their activity. Herein, a crystal regulation strategy induced by nitrogen doping is developed to construct interconnected Mn oxide nano-particles/rods (N-MnO x -Y) with different contents of [MnO 6 ] octahedron for ORR. In N-MnO x -Y, "Y" refers to the mass ratio of melamine to α-MnO 2 nanorods during calcination. Nitrogen doping induced increased content of crystalline [MnO 6 ] octahedron is the primary factor boosting the intrinsic activity of N-MnO x -Y. The overall activity of N-MnO x -Y is also determined by electrochemically active area (ECSA) which is closely related to nitrogen doping. The crystal optimal N-MnO x -30 with high content of crystalline [MnO 6 ] octahedron and large ECSA exhibits the highest half-wave potential for ORR and the largest kinetic current density (j k ) among the N-MnO x -Y catalysts. When used as a cathodic catalyst, a homemade zinc-air battery driven by N-MnO x -30 delivers a peak power density higher than the one driven by Pt/C, along with better rate performance and a larger discharging specific capacity. This impressive electrocatalytic performance of N-MnO x -30 superior to Pt/C originates from the synergistic effect between crystalline [MnO 6 ] octahedron, active area exposure, oxygen vacancy, Mn-N sites, and the three-dimensional hierarchical structure, which benefiting electronic/mass transmission and structural stability. This work offers a feasible strategy for constructing hierarchical and crystal tunable metal oxides electrocatalysts for efficient energy conversion.

Enhanced oxygen reduction activity of α-MnO2 by NH3 plasma treatment

Enhancing oxygen reduction activity of α-MnO2 by defect-engineering and N doping through plasma treatments

Mesoporous MnO2 nanosheets for efficient electrocatalytic nitrogen reduction via high spin polarization induced by oxygen vacancy

Bismuth-doped Manganese Molybdenum Bimetallic Oxide Nanorods As a Highly Efficient Nitrogen Reduction Catalyst

MnO2 nanoarray with oxygen vacancies: An efficient catalyst for NO electroreduction to NH3 at ambient conditions

Plasma-Assisted Synthesis of Defect-Rich O and N Codoped Carbon Nanofibers Loaded with Manganese Oxides as an Efficient Oxygen Reduction Electrocatalyst for Aluminum–Air Batteries

Nitrogen doping regulates microcrystal structure of interconnected Mn oxide particles/rods for oxygen reduction electrocatalysis

Abundant Oxygen Vacancies Induced by the Mechanochemical Process Boost the Low-Temperature Catalytic Performance of MnO2 in NH3-SCR

A simple hydrothermal synthesis of oxygen vacancy-rich MnMoO4 rod-like materials and its highly efficient electrocatalytic nitrogen reduction

Modulating Oxygen Vacancies of TiO2 Nanospheres by Mn-Doping to Boost Electrocatalytic N2 Reduction

Introducing oxygen vacancies in a bi-metal oxide nanosphere for promoting electrocatalytic nitrogen reduction

Oxygen-Coordinated Single Mn Sites for Efficient Electrocatalytic Nitrate Reduction to Ammonia

Modulating Oxygen Vacancies of TiO 2 Nanospheres by Mn-Doping to Boost Electrocatalytic N 2 Reduction

Experimental and Theoretical Investigation of Mesoporous MnO2 Nanosheets with Oxygen Vacancies for High-Efficiency Catalytic DeNO(x)

Mn-modified nitrogen-doped Pt-based electrocatalyst for efficient oxygen reduction in aluminum-air batteries

Trace Cr(OH)3 modified α-MnO2 electrocatalyst intercalated by Ag+ with superior activity and stability for oxygen reduction reaction

Tuning the Pt-N coordination in Pt/MOFs nanosheets under N 2 plasma for enhanced oxygen reduction reaction

N/P-doped NiFeV oxide nanosheets with oxygen vacancies as an efficient electrocatalyst for the oxygen evolution reaction

Efficient Ammonia Production Beginning from Enhanced Air Activation

Functionalized nitrogen doping induced manganese oxyhydroxide rooted in manganese sesquioxide rod for robust oxygen reduction electrocatalysis

MnN4 Oxygen Reduction Electrocatalyst: Operando Investigation of Active Sites and High Performance in Zinc–Air Battery