Manipulating morphology and surface engineering of spinel cobalt oxides to attain high catalytic performance for propane oxidation

Wenjun Zhu,Xiao Chen,Chuang Li,Zhongmin Liu,Changhai Liang

DOI: https://doi.org/10.1016/j.jcat.2021.02.014

IF: 7.3

2021-04-01

Journal of Catalysis

Abstract:<p>The selective synthesis of nanomaterials with different morphologies and crystal facets is of great significance for catalytic properties and practical applications. Herein, we report a strategy for controllable fabrication of hierarchical Co₃O₄ materials with various morphologies (ellipsoidal, flower-like, book-shaped, spindle-like), and their catalytic properties in propane oxidation are studied. Co₃O₄-B (book-shaped) is found to exhibit the highest propane oxidation rate (0.86×10^-8 mol m^-2 s^-1) and the highest turnover frequency (TOF=11.49×10⁻³ s^-1) at 220 °C. It confirms that Co₃O₄-B provides a higher specific surface area, highly exposed {110} facet and abundant Co³⁺ cations, which make the catalyst exhibit favorable low-temperature reducibility and oxygen mobility, and thus improves the catalyst activity. In situ DRIFTS analysis reveals that the intermediates such as, carboxylate and carbonate species, are involved in propane oxidation. Furthermore, Co₃O₄-B shows great water-resistance performance, and no significant deactivation is observed after long-term stability and reusability tests.</p>

chemistry, physical,engineering, chemical

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to improve the catalytic performance of spinel cobalt oxide ($\text{Co}_3\text{O}_4$) in the propane oxidation reaction through regulating its morphology and surface engineering. Specifically, the researchers designed and synthesized $\text{Co}_3\text{O}_4$ materials with different morphologies (ellipsoidal, flower - like, book - like, spindle - like) and explored the catalytic activity and mechanism of these materials in propane oxidation. The study found that book - like $\text{Co}_3\text{O}_4$ ($\text{Co}_3\text{O}_4$-B) exhibited the highest propane oxidation rate ($0.86\times 10^{-8} \text{mol}\cdot\text{m}^{-2}\cdot\text{s}^{-1}$) and the highest turnover frequency (TOF = $11.49\times 10^{3}\text{s}^{-1}$), which was attributed to its relatively high specific surface area, highly exposed {110} crystal planes and abundant $\text{Co}^{3+}$ ions. These characteristics made it excellent in low - temperature reducibility and oxygen mobility, thereby enhancing the catalytic activity. In addition, $\text{Co}_3\text{O}_4$-B also showed good water vapor resistance, and no significant deactivation was observed in long - term stability and reusability tests.