Abstract:A Polymer electrolyte membrane fuel cell (PEMFC) is one of the most important applications for decarbonization of energy using hydrogen as an energy source and is considered a promising future power source due to its high efficiency, low operating temperature, fast startup, and low noxious emissions. In particular, improvement in durability of PEMFC is one of the major issues to spur the commercialization of the PEMFC system. Therefore, to improve the durability of PEMFC systems, diagnostic strategies are required to identify faulty conditions of PEMFC systems such as fuel starvation, dehydration, flooding, load cycling, and startup-shutdown (SU/SD). The problematic form of the membrane electrode assembly (MEA) that causes a decrease in the performance of PEMFCs in steady-state and dynamic operating conditions includes Pt dissolution, ionomer degradation, carbon corrosion [1] , and mechanical problems of the membrane in some circumstances. Among them, the undesired corrosion reaction, namely, the electrochemical carbon oxidation reaction, results in a drastic decrease in electrochemical double layer capacitance (EDLC), generation of oxygen functional groups in carbon supports, and severe electrochemical surface area (ECSA) fading [2, 3], followed by deteriorated PEMFC performance. Typically, the high potential inducing carbon corrosion reactions would occur during SU/SD and fuel starvation conditions. In detail, as for fuel starvation, a temporary shortage of H 2 supply to one or several cells in a PEMFC stack causes the cell voltage reversal, accompanied by a potential strike over 1.0 V vs. RHE (Figure 1) with significant electrode degradation [4 , 5]. Also, the generation of hydrogen/air boundary at the anode due to the gas crossover through the membrane results in a high potential (~1.4 V vs. RHE), accelerating the decomposition of carbon support [6]. Therefore, in this work, to investigate the effects of high potential inducing electrode degradation on PEMFC performance, we conducted accelerated stress tests (AST), and in particular, we studied the correlation between electrode degradation behaviors as well as structural properties of porous carbon such as ionic resistance, EDLC with PEMFC performance in the systemic point of view. Specially, we could see the contrasting degradation behaviors and various performance decay rates using electrochemical impedance spectroscopy (EIS) analysis. EIS can be used to isolate the contribution of many processes to performance loss, allowing investigation of the effect of carbon corrosion-induced catalyst layer changes on fuel cell performance [ 7]. The measured EIS data is evaluated through the parametric fitting of the transmission line model (TLM) to the EIS spectrum. In addition, relaxation time distribution (DRT) analysis for direct analysis of internal resistance factors by reinforcing the TLM-based impedance analysis results was applied as a diagnostic method to evaluate electrode degradation. During the ASTs, electrochemical measurements (i-V, CV, LSV, and EIS) were performed to estimate the degree of PEMFC degradation, we also conducted ex-situ surface analysis of MEA using SEM, TEM, and XPS to elucidate the specific degradation components. References [1] Sorrentino, Antonio, Kai Sundmacher, and Tanja Vidakovic-Koch. "Polymer electrolyte fuel cell degradation mechanisms and their diagnosis by frequency response analysis methods: a review." Energies 13.21 (2020): 5825. [2] Macauley, Natalia, et al. "Carbon corrosion in PEM fuel cells and the development of accelerated stress tests." Journal of The Electrochemical Society 165.6 (2018): F3148. [3] Kwon, JunHwa, et al. "Identification of electrode degradation by carbon corrosion in polymer electrolyte membrane fuel cells using the distribution of relaxation time analysis." Electrochimica Acta (2022): 140219. [4] Bentele, D., et al. "PEMFC Anode Durability: Innovative Characterization Methods and Further Insights on OER Based Reversal Tolerance." Journal of The Electrochemical Society 168.2 (2021): 024515. [5] Tovini, Mohammad Fathi, et al. "Degradation mechanism of an IrO2 anode co-catalyst for cell voltage reversal mitigation under transient operation conditions of a PEM fuel cell." Journal of The Electrochemical Society 168.6 (2021): 064521. [6] Bisello, Andrea, et al. "Mitigated Start-Up of PEMFC in Real Automotive Conditions: Local Experimental Investigation and Development of a New Accelerated Stress Test Protocol." Journal of The Electrochemical Society 168.5 (2021): 054501. [7] Kwon, JunHwa, et al. "A Comparison Study on the Carbon Corrosion Reaction under Saturated and Low Relative Humidity Conditions via Transmission Line Model-Based Electrochemical Impedance Anal -Abstract Truncated-

Comprehensive analysis of recovery procedures for SO 2 -contaminated proton exchange membrane fuel cells

Analysis of Electrode Degradation By High-Potential Environment-Using Electrochemical Impedance Spectroscopy in Polymer Electrolyte Membrane Fuel Cells

Studying the Effect of Operating Conditions and NO2 Cathode Contamination on PEM Fuel Cells Using Distribution Function of Relaxation Times Analysis

Air Bleeding Strategies to Increase the Efficiency of Proton Exchange Membrane Fuel Cell Stationary Applications Fuelled with CO ppm-levels

Deactivated Pt Electrocatalysts for the Oxygen Reduction Reaction: The Regeneration Mechanism and a Regenerative Protocol

In-Depth Understanding of Oxygen Transfer in the Catalyst Layer of High-Temperature Proton Exchange Membrane Fuel Cells

Mitigation of Performance Degradation of Cathodes for Polymer Electrolyte Membrane Fuel Cells

Quantification of effects of performance recovery procedures for polymer electrolyte membrane fuel cells

Pt/C-TiO2 as Oxygen Reduction Electrocatalysts against Sulfur Poisoning

Investigation of real-time changes and recovery of proton exchange membrane fuel cell in voltage reversal

Analysis of Sulfur Poisoning on a PEM Fuel Cell Electrode

Localized Electrochemical Performance Degradation in Polymer Electrolyte Fuel Cells (PEFCs)

Recreating Fuel Cell Catalyst Degradation in Aqueous Environments for Identical-Location Scanning Transmission Electron Microscopy Studies

CO-tolerance behaviors of proton exchange membrane fuel cell stacks with impure hydrogen fuel

Bifunctional Electrocatalyst Materials for Improved Cell Reversal Tolerance in PEM Fuel Cell

Degradation mechanisms of proton exchange membrane fuel cell under typical automotive operating conditions

Recovery characteristics of reversible degradation for proton exchange membrane fuel cell stack under accelerated stress test

Operando deconvolution of the degradation mechanisms of iron–nitrogen–carbon catalysts in proton exchange membrane fuel cells

Ultralow Platinum Loading Proton Exchange Membrane Fuel Cells: Performance Losses and Solutions

Electrocatalyst Durability under Simulated Automotive Drive Cycles