Abstract:To avoid an enormous energy crisis in the not-too-distant future, it be emergent to establish high-performance energy storage devices such as supercapacitors. For this purpose, a three-dimensional (3D) heterostructure of Co3 O4 and Co3 S4 on nickel foam (NF) that is covered by reduced graphene oxide (rGO) has been prepared by following a facile multistep method. At first, rGO nanosheets are deposited on NF under mild hydrothermal conditions to increase the surface area. Subsequently, nanowalls of cobalt oxide are electro-deposited on rGO/Ni foam by applying cyclic-voltammetry (CV) under optimized conditions. Finally, for the synthesis of Co3 O4 @Co3 S4 nanocomposite, the nanostructure of Co3 S4 was fabricated from Co3 O4 nanowalls on rGO/NF by following an ordinary hydrothermal process through the sulfurization for the electrochemical application. The samples are characterized by using X-ray diffraction (XRD) and scanning electron microscopy (SEM). The obtained sample delivers a high capacitance of 13.34 F cm-2 (5651.24 F g-1 ) at a current density of 6 mA cm-2 compared to the Co3 O4 /rGO/NF electrode with a capacitance of 3.06 F cm-2 (1230.77 F g-1 ) at the same current density. The proposed electrode illustrates the superior electrochemical performance such as excellent specific energy density of 85.68 W h Kg-1 , specific power density of 6048.03 W kg-1 and a superior cycling performance (86% after 1000 charge/discharge cycles at a scan rate of 5 mV s-1 ). Finally, by using Co3 O4 @Co3 S4 /rGO/NF and the activated carbon-based electrode as positive and negative electrodes, respectively, an asymmetric supercapacitor (ASC) device was assembled. The fabricated ASC provides an appropriate specific capacitance of 79.15 mF cm-2 at the applied current density of 1 mA cm-2 , and delivered an energy density of 0.143 Wh kg-1 at the power density of 5.42 W kg-1 .

Binder-free copper manganese sulfide nanoflake arrays electrodeposited on reduced graphene oxide-wrapped nickel foam as an efficient battery-type electrode for asymmetric supercapacitors

A Zinc Cobalt Sulfide Nanosheet Array Derived from a 2D Bimetallic Metal-Organic Frameworks for High-Performance Supercapacitors

A Metal-Organic Framework Derived Hierarchical Nickel-Cobalt Sulfide Nanosheet Array on Ni Foam with Enhanced Electrochemical Performance for Supercapacitors

NiCo2S4@Ni3S2 Hybrid Nanoarray on Ni Foam for High-Performance Supercapacitors

Rapid Synthesis of Mn-Doped NiFe2O4 Nanosheet Arrays for High-Performance Hybrid Supercapacitors

One-step colloid fabrication of nickel phosphides nanoplate/nickel foam hybrid electrode for high-performance asymmetric supercapacitors

Enhanced Supercapacitor Performance Using a Co3 O4 @Co3 S4 Nanocomposite on Reduced Graphene Oxide/Ni Foam Electrodes

Revolutionizing energy storage with advanced reduced graphene oxide-wrapped MnSe@CoSe@FeSe2 nanowires

Electrodeposition of Manganese-Nickel-Cobalt Sulfides on Reduced Graphene Oxide/Nickel Foam for High-Performance Asymmetric Supercapacitors

Facile synthesis of neuronal nickel-cobalt-manganese sulfide for asymmetric supercapacitors with excellent energy density

Design and fabrication of free-standing Ni3S2/NiV-LDH nanosheets arrays on reduced graphene oxide/Ni foam as a novel electrode for asymmetric supercapacitor

Synthesis of binder-free nanofibers ZnS/MoS2/NiF electrode material for asymmetric supercapacitor applications

High performance NiCo-LDH//Fe2O3 asymmetric supercapacitors based on binder-free electrodes with dual conductive networks

Nanoflower-like Cu 2 CoSnS 4 grown on nickel foam as binder-free electrode material for asymmetric supercapacitors with high rate and capacitance

Synergistic coupling of MnS/Ni3S2 and Co(OH)2 nanosheets as binder-free electrode materials for asymmetric supercapacitors with enhanced performance

Sodium 5-Sulfosalicylate-assisted Hydrothermal Synthesis of a Self-Supported Co3S4−Ni3S2@nickel Foam Electrode for All-Solid-state Asymmetric Supercapacitors

Electrodeposited coral-like bimetallic NiCo-MOFs on Ni foam as binder-free electrodes for high performance all solid-state asymmetric supercapacitors

Facile Synthesis of Neuronal Nickel-Cobalt-Manganese Sulfide for Asymmetric Supercapacitors with High Energy Density

Double‐Layer MnCo2S4@Ni‐Co‐S Core/Shell Nanostructure on Nickel Foam for High‐Performance Supercapacitor

Constructing metal organic framework derived manganese cobalt layered double hydroxide nanosheets on Ni foam as cost-effective binder-free electrodes of high-performance supercapacitors

Synergistic electrochemical behaviour of hydrothermally deposited Ni·Co LDH/rGO nanocomposite on nickel foam