Modulating vacancies in nonstoichiometric oxides by annealing polarized nanoporous NiCoMn as thick pseudocapacitive electrode

Hongwei Li,Shaofei Zhang,Hao Liu,Zhijun Qiao,Zhenyang Yu,Zhijia Zhang,Jianxin Li,Jianli Kang

DOI: https://doi.org/10.1016/j.electacta.2020.137628

IF: 6.6

2021-02-01

Electrochimica Acta

Abstract:<p>Thick nanoporous electrode design with pore size in several nanometers can substantially improve the active sites to achieve high energy density. However, the sluggish ion/charge kinetics and mechanical instability limit their rate and long-term cycling capability. To address these obstacles, herein, a thick vacancy-riched nanoporous oxides (V_o) core-shell structure as pseudocapacitive electrode in alkaline electrolyte was prepared by polarizing a nanoporous NiCoMn alloy and subsequently mild annealing in Ar atmosphere. As a result, a large number of coordination unsaturated sites can be exposed on active oxide layer by mild annealing. Meanwhile, the nanopores can be coarsened to tens of nanometers. The coordination unsaturated sites synergy with coarsened nanopores can not only endow high-efficient ion/electrons transport channels but also hold the structure stable during fast charge/discharge process. Electrochemical performance characterization illustrates that the 4V_o electrode annealed at 400°Cshows high capacity retention of about 69.7% at current rates from 1 A cm⁻³ to upward of 10 A cm⁻³ (1464 C cm⁻³ at 1 A cm⁻³ and 908 C cm⁻³ at 10 A cm⁻³) and high energy density of 90.7 mWh cm⁻³, demonstrating a potential application in pseudocapacitors. More importantly, the novel structural design exhibits promising prospects toward the practical application of integrated thick electrodes.</p>

electrochemistry