Microscopic Insight into Ruthenium Exsolution from LaFe 0.9 Ru 0.1 O 3 Perovskite

Yu Wang,Paul Paciok,Lukas Pielsticker,Wei Wang,Alexander Spriewald Luciano,Min Ding,Lorena Glatthaar,Walid Hetaba,Yanglong Guo,Jaime Gallego,Bernd M. Smarsly,Herbert Over

DOI: https://doi.org/10.1021/acs.chemmater.4c01084

IF: 10.508

2024-06-10

Chemistry of Materials

Abstract:Metal exsolution is a smart strategy that allows modification and enrichment of a material’s surface with highly active catalytic phases, thus offering the possibility to fine-tune the surface chemical composition. We study the exsolution of Ru from a perovskite solid solution LaFe0.9Ru0.1O3 (LFRO) to form Ru nanoparticles and their passivation by a conforming LaO x layer by applying a variety of in situ techniques, including TEM and XPS, in combination with ex situ infrared and Raman spectroscopy, but most notably by utilizing the catalytic propane combustion to probe the formation of the passivating LaO x layer. During the Ru exsolution process, Ru3+ in LFRO is reduced first to the Ruβ species and subsequently into a Ru0 species, evidencing the exsolution of Ru particle. The transformation of Ru3+ → Ruβ proceeds already below 300 °C and is correlated with the formation of oxygen vacancies under a reductive atmosphere. The subsequent transformation of Ruβ toward Ru0 needs at least a reduction temperature of 400 °C that is likely to be determined by the diffusion of Ru3+ from the near-surface region of LFRO toward the surface. Only above 600 °C ruthenium cations from the bulk of LFRO are exsolved, leading to the further growth of Ru particles. Around 600 °C, the exsolution of Ru particles is accompanied by the formation of a covering LaO x layer. We propose that La segregation and precipitation as surface LaO x are driven by the overstoichiometry of La in LFRO after Ru exsolution.

materials science, multidisciplinary,chemistry, physical