Optimization of biomass-to-water ratio and glycerol content to develop antioxidant- enriched bioplastics from whole seaweed biomass of Kappaphycus sp.

Eunice Lua Hanry,Noumie Surugau

DOI: https://doi.org/10.1007/s10811-024-03197-y

2024-02-20

Journal of Applied Phycology

Abstract:Pollution caused by petroleum-based plastics, especially single-use food packaging, has become a global problem. In order to offer sustainable alternatives to traditional plastic, it is important to explore the use of new biodegradable plastic materials made from renewable sources. Bioplastics made from seaweed extracts, such as carrageenan and alginate, show promise as viable options. However, these phycocolloids are expensive and require a lengthy extraction process. This report presents the development of bioplastics using the entire biomass of a red seaweed ( Kappaphycus sp.). The initial focus of the study was to optimize the concentration of the main ingredients, which included biomass and glycerol (plasticizer agent). The concentration range that was tested included a biomass-to-water ratio of 1:50 to 1:90 and a plasticizer concentration of 1% to 5% ( v/v ). Subsequently, bioplastics were created by incorporating natural dye extracts from butterfly pea flower ( Clitoria ternatea ), bougainvillea flower ( Bougainvillea glabra ), and dragon fruit peel ( Hylocereus polyrhizus ) using a casting method at the selected optimum concentrations. The resulting bioplastics were then characterized for their physicochemical properties (including shelf-life and biodegradability), and antimicrobial activity using standard methods. The study successfully developed bioplastics with a thickness of less than 100 μm and a moisture content below 40%. Within the tested range, the most optimal concentrations were a biomass-to-water ratio of 1:50 to 1:60 and 1% glycerol, based on factors such as tensile strength (TS), water vapor transmission rate (WVTR), elasticity, appearance, shelf-life, and biodegradability. All of the bioplastics completely degraded during a soil burial test within 13-15 days. The inclusion of brightly coloured plant extracts increased the bioplastics' antioxidant properties by more than 10% in scavenging activity. Furthermore, the dyed bioplastics had a shelf-life that was 20-30% longer. While these biomass bioplastics have lower tensile strength, elasticity, and water vapor permeation rate (<10 MPa, 2 g m -2 h -1 , respectively), they show potential for applications where high tensile strength is not required, such as food packaging or wrapping.

biotechnology & applied microbiology,marine & freshwater biology