Farnoush Ahmadpour,Fatemeh Ganjali,Fateme Radinekiyan,Reza Eivazzadeh-Keihan,Milad Salimibani,Hossein Bahreinizad,Mohammad Mahdavi,Ali Maleki
Abstract:Herein, a new magnetic nanobiocomposite based on a synthesized cross-linked pectin–cellulose hydrogel (cross-linked Pec–Cel hydrogel) substrate was designed and synthesized. The formation of the cross-linked Pec–Cel hydrogel with a calcium chloride agent and its magnetization process caused a new and efficient magnetic nanobiocomposite. Several spectral and analytical techniques, including FTIR, SEM, VSM, TGA, XRD, and EDX analyses, were performed to confirm and characterize the structural features of the magnetic cross-linked pectin–cellulose hydrogel nanobiocomposite (magnetic cross-linked Pec–Cel hydrogel nanobiocomposite). Based on SEM images, prepared Fe 3 O 4 magnetic nanoparticles (MNPs) were uniformly dispersed in the Pec–Cel hydrogel context, representing an average particle size between 50.0 and 60.0 nm. The XRD pattern also confirms the crystallinity of the magnetic nanobiocomposite. All constituent elements and their distribution have been depicted in the EDX analysis of the magnetic nanobiocomposite. VSM curves confirmed the superparamagnetic behavior of Fe 3 O 4 MNPs and the magnetic nanobiocomposite with a saturation magnetization of 77.31 emu g −1 and 48.80 emu g −1 , respectively. The thermal stability of the nanobiocomposite was authenticated to ca. 800 °C based on the TGA thermogram. Apart from analyzing the structural properties of the magnetic cross-linked Pec–Cel hydrogel nanobiocomposite, different concentrations (0.5 mg mL −1 , 1.0 mg mL −1 , 2.0 mg mL −1 , 5.0 mg mL −1 , and 10.0 mg mL −1 ) of this new magnetic nanostructure were exposed to an alternating magnetic field (AMF) at different frequencies (100.0 MHz, 200.0 MHz, 300.0 MHz, and 400.0 MHz) to evaluate its capacity for an in vitro hyperthermia process; in addition, the highest specific absorption rate (126.0 W g −1 ) was obtained by the least magnetic nanobiocomposite concentration (0.5 mg mL −1 ).
What problem does this paper attempt to address?
This paper aims to solve the problems of in - vitro hyperthermia technology in cancer treatment. Specifically, the researchers designed and synthesized a new magnetic nanobiocomposite based on pectin - cellulose hydrogel (cross - linked Pec –Cel hydrogel). This material, through Fe\(_3\)O\(_4\) magnetic nanoparticles (MNPs) evenly dispersed in the hydrogel matrix, exhibits excellent magnetic and thermal properties and is suitable for in - vitro hyperthermia applications.
### Research Background and Objectives
In recent years, hydrogels with specific three - dimensional network structures have attracted attention due to their properties such as elasticity, biodegradability, biocompatibility, reversibility, and water - absorption capacity. In particular, hydrogels based on natural polymers, such as pectin and cellulose, are more popular in green chemistry because of their biodegradability, biocompatibility, and low toxicity. The research objective of this paper is to develop a new magnetic nanobiocomposite for in - vitro hyperthermia in cancer treatment.
### Main Research Contents
1. **Material Synthesis**:
- Prepared cross - linked pectin - cellulose hydrogel (cross - linked Pec –Cel hydrogel), using calcium chloride as a cross - linking agent.
- In this hydrogel matrix, Fe\(_3\)O\(_4\) magnetic nanoparticles (MNPs) were prepared by in - situ synthesis method, forming a magnetic nanobiocomposite.
2. **Material Characterization**:
- The structural characteristics of the magnetic nanobiocomposite were characterized using multiple spectroscopic and analytical techniques (FTIR, SEM, VSM, TGA, XRD, and EDX).
- Confirmed the uniform distribution of Fe\(_3\)O\(_4\) MNPs in the hydrogel, with an average particle size between 50.0 and 60.0 nm.
- The superparamagnetic behavior of Fe\(_3\)O\(_4\) MNPs and the magnetic nanobiocomposite was confirmed by VSM curves, and the saturation magnetization intensities were 77.31 emu g\(^{-1}\) and 48.80 emu g\(^{-1}\), respectively.
- TGA thermogravimetric analysis showed that the thermal stability of the nanobiocomposite can reach about 800°C.
3. **In - vitro Hyperthermia Performance Evaluation**:
- Magnetic nanobiocomposites at different concentrations (0.5 mg mL\(^{-1}\), 1.0 mg mL\(^{-1}\), 2.0 mg mL\(^{-1}\), 5.0 mg mL\(^{-1}\), and 10.0 mg mL\(^{-1}\)) were tested for in - vitro hyperthermia performance under alternating magnetic fields (AMF) at different frequencies (100.0 MHz, 200.0 MHz, 300.0 MHz, and 400.0 MHz).
- The results showed that the magnetic nanobiocomposite at the lowest concentration (0.5 mg mL\(^{-1}\)) exhibited the highest specific absorption rate (SAR) under AMF, reaching 126.0 W g\(^{-1}\).
### Conclusion
The research results show that this new magnetic nanobiocomposite has a high saturation magnetization intensity and good thermal properties, and is suitable for in - vitro hyperthermia. In particular, the magnetic nanobiocomposite at a lower concentration exhibits a higher specific absorption rate under an alternating magnetic field, showing its potential application value in cancer treatment. Future research can further study its effect in clinical applications.