Abstract:Spheroidized ferrite-cementite steel (SFC) is susceptible to micro-defects owing to the mismatched deformation between the ferrite and cementite during cold forming, which seriously deteriorates the fatigue life. However, the damage mechanism related to microstructural features in the SFC steel during cold deformation has not been fully investigated, hindering control of the microstructure and forming process. This study presents a method coupled with experiments and multiscale simulations to research the damage mechanisms and the dependence of microstructure features under uniaxial tension in SFC steel. In situ tensile test revealed three damage mechanisms in SFC steel under uniaxial tension: cementite cracking, ferrite/cementite interface debonding, and ferrite cracking. In particular, the final fracture was mainly dominated by the ferrite/cementite interface debonding. In multiscale simulations, the macroscale tensile and nanoindentation simulations were carried out to obtain the strain history and mechanical properties of the mesoscale simulations, respectively. The mesoscale IP-based RVE and CP-based unit cells simulations were performed to capture the driving forces from the three damage mechanisms and the dependence of microstructural features, respectively. The nanoscale molecular dynamics simulation was conducted to identify the model parameters of cohesive zone model (CZM) in the mesoscale simulations. The numerical results indicated that particle-cracking void occurred when the internal von Mises stress exceeded the ultimate strength of the cementite particles. Interface-debonding void nucleated when the load on the particle was insufficient to resist its strength. Matrix-cracking should be attributed to the stress concentration caused by the dislocation pile-up or the crossing of multiple slip bands. In addition, interfacial debonding were more likely to occur in the stable orientations and high-angle grain boundaries of ferrite matrix. Compared with a circular cementite particle, an elliptical particle was more prone to cause interfacial debonding. Also, the ferrite/ferrite grain boundary showed earlier interfacial debonding perpendicular to the loading direction than parallel to the loading direction.

Investigation of orientation coefficient on meso-damage evolution of steel fiber-reinforced cement composites

Stochastic Fracture of Concrete Composites: A Mesoscale Methodology

Concurrent Multiscale Modeling of In-Plane Micro-Damage Evaluation in Z-pinned Composite Laminates

Mesoscale modeling of flexural fracture behavior in steel fiber reinforced concrete

3D meso-scale modelling of tensile and compressive fracture behaviour of steel fibre reinforced concrete

A Mesoscale Modelling Approach Coupling SBFEM, Continuous Damage Phase-Field Model and Discrete Cohesive Crack Model for Concrete Fracture

Study on multi-scale damage and failure mechanism of steel fiber reinforced concrete: Experimental and numerical analysis

Stress–Strain Behavior of FRC in Uniaxial Tension Based on Mesoscopic Damage Model

Investigation on Mechanical and Microstructure Properties of Steel Fiber Reinforced Concrete

Influence of fiber orientation on the microstructures of interfacial transition zones and pull-out behavior of steel fiber in cementitious composites

Investigation of damage mechanisms related to microstructural features of ferrite-cementite steels via experiments and multiscale simulations

Experiment and mesoscopic modelling on the dynamic compressive behaviors of a new carbon fiber-reinforced cement-based composite

A 3D Cohesive‐frictional Coupled Interface Model for Mesoscale Simulation of Steel Fibre‐reinforced Concrete

3D meso-scale investigation of ultra high performance fibre reinforced concrete (UHPFRC) using cohesive crack model and Weibull random field

3D Mesoscale Fracture Analysis of Concrete under Complex Loading

A micromechanical crack bridging model considering the slip-softening interface with the residual shear stress for SFRCC

3D mesoscale modelling of steel fiber-reinforced aggregate concrete

Computational technology for analysis of 3D meso-structure effects on damage and failure of concrete

Effect of Stochastic Loading on Tensile Damage and Fracture of Fiber-Reinforced Ceramic-Matrix Composites

A Multiphase Mesostructure Mechanics Approach to the Study of the Fracture-Damage Behavior of Concrete

Investigation on fracture behaviour of UHPFRC using a mesoscale computational framework