Melting of Carbonated Pelite at 5.5–15.5 GPa: Implications for the Origin of Alkali-Rich Carbonatites and the Deep Water and Carbon Cycles
Chen, Xueqian,Wang, Meili,Inoue, Toru,Liu, Qiong,Zhang, Lifei,Bader, Thomas
DOI: https://doi.org/10.1007/s00410-021-01867-5
IF: 4.1068
2022-01-01
Contributions to Mineralogy and Petrology
Abstract:Melting experiments on a carbonated pelite were performed at 5.5–15.5 GPa, 800–1875 °C using multi-anvil apparatuses to determine the melting phase relations and the P–T stability fields of various phases, which may shed some light on the source of silica-undersaturated magmas and the deep Earth carbon and water cycles. The subsolidus assemblages contain garnet, clinopyroxene, coesite/stishovite at all investigated pressures. Phengite, aragonite or magnesite, and topaz-OH occur below 9.5 GPa. Phase egg, K-hollandite, Ti-oxide, and CAS phase appear at 12–15.5 GPa. Phengite is stable up to 6 GPa and 800 °C, with the phengite-out boundary overlapping with the carbonate-out curve. Thus, the initial melt is carbonatitic and extremely potassium-rich, with K2O/Na2O weight-ratios larger than 40 at fluid-present conditions. The melting reaction phase egg + magnesite + aragonite + (clinopyroxene) + stishovite → melt + garnet + kyanite defines the solidus at 9.5 GPa, 1000–1100 °C. With increasing pressure, the composition of the near-solidus melts gradually evolves from potassium-rich to sodium-rich due to the formation of K-hollandite and the destabilization of clinopyroxene, and as a result of the clinopyroxene-out, the near-solidus melt has the lowest K2O/Na2O value and partitioning coefficient of sodium between clinopyroxene and melt $$\left( {D_{{{\text{Na}}}}^{{\text{cpx/melt}}} } \right)$$ at 15.5 GPa. In addition, phase egg remains stable up to 1400 °C at 15.5 GPa. Thus, phase egg is a good candidate as a deep-water carrier during subduction of pelitic sediments. This study concludes that low degree partial melting of carbonated pelite produces alkali-rich carbonatite melts evolving from potassium-rich (6–12 GPa) to sodium-rich (above 12 GPa) with increasing pressure, and if a slab stagnates at depth, and/or subduction slows down, the produced carbonatite melts will be more silicate-rich with increasing temperature. Moreover, the produced melts generally evolve from relatively silicate-rich to carbonatite-rich with increasing pressure. These alkali-rich carbonatite melts are compositionally similar to those in diamond inclusions, which provides strong evidence for the origin of deep-seated silica-undersaturated carbonatitic magma. Such magma is an ideal metasomatic agent that can give rise to mantle heterogeneity.