Abstract:Synthesis experiments were conducted in the quaternary system K2O–Na2O–CaO–SiO2, resulting in the formation of a previously unknown compound with the composition K0.72Na1.71Ca5.79Si6O19. Single crystals of sufficient size and quality were recovered from a starting mixture with a K2O:Na2O:CaO:SiO2 molar ratio of 1.5:0.5:2:3. The mixture was confined in a closed platinum tube and slowly cooled from 1150°C at a rate of 0.1°C min−1 to 700°C before being finally quenched in air. The structure has tetragonal symmetry and belongs to space group P4122 (No. 91), with a = 7.3659 (2), c = 32.2318 (18) Å, V = 1748.78 (12) Å3, and Z = 4. The silicate anion consists of highly puckered, unbranched six-membered oligomers with the composition [Si6O19] and point group symmetry 2 (C2). Although several thousands of natural and synthetic oxosilicates have been structurally characterized, this compound is the first representative of a catena-hexasilicate anion, to the best of our knowledge. Structural investigations were completed using Raman spectroscopy. The spectroscopic data was interpreted and the bands were assigned to certain vibrational species with the support of density functional theory at the HSEsol level of theory. To determine the stability properties of the novel oligosilicate compared to those of the chemically and structurally similar cyclosilicate combeite, we calculated the electronegativity of the respective structures using the electronegativity equalization method. The results showed that the molecular electronegativity of the cyclosilicate was significantly higher than that of the oligostructure due to the different connectivities of the oxygen atoms within the molecular units.

Ba3Zn4Si4O15: A Novel Centrosymmetric Silicate with Isolated SiO4 and Si2O7 Units

Ba5Y12Zn[O(SiO4)]8: A Novel Non-Centrosymmetric Silicate with a Short Ultraviolet Cut-off Edge Featuring [ZnSi4O16] and [SiO4] Units

Ba 2 ScBSi 2 O 9 : A Mixed-Coordination Borosilicate with a Low B/Si Ratio Exhibiting Enhanced Second Harmonic Generation Response

Properties and Crystal Structure of A Novel Silicate Single Crystal: Bah2sio4

Synthesis, Crystal Structure and Characterization of the Barium Zinc Tellurate Disilicate: Ba3Zn6[TeO6] [Si2o7]2.

Synthesis , Crystal Structure and Characterization of the Barium Zinc Tellurate Disilicate

Syntheses, Characterization, and Optical Properties of Centrosymmetric Ba3(BS3)1.5(MS3)0.5 and Noncentrosymmetric Ba3(BQ3)(SbQ3).

Quaternary sulfide Ba6Zn6ZrS14: synthesis, crystal structure, band structure, and multiband physical properties

Synthesis and Structure Determination of SCM-15: a 3D Large-Pore Zeolite with Interconnected Straight 12×12×10-Ring Channels

Sn2SiS4, Synthesis, Structure, Optical and Electronic Properties

Structure Elucidation and Computationally Guided Synthesis of SSZ‐43: A One‐Dimensional 12‐ring Zeolite with Unique Sinusoidal Channels

BaZnBe 2 (BO 3 ) 2 F 2 : a novel zinc-beryllium borate with SBBO-type structure overcoming the polymorphism problem

K0.72Na1.71Ca5.79Si6O19 – the first oligosilicate based on [Si6O19]-hexamers and its stability compared to cyclosilicates

Synthesis, Crystal Structure, and Optical Properties of Noncentrosymmetric Na2ZnSnS4.

Ba2Cd(B3O6)2: A congruent-melting compound with isolated B3O6 units

Synthesis, Crystal Structure and Optical Properties of a Novel Sodium Lead Pentaborate, NaPbB5O9

Solvothermal Synthesis and Crystal Structure of Zn(en)_ 3B_ 5O_ 7(OH)_ 3

Synthesis And Crystal Structure Of [{Zn(3-Sba)(2,2 '-Bipy)(H2o)(2)}Center Dot H2o](N)

Synthesis, structure and property studies of a new series of rare earth (Ce, Tb) bismuth silicates

Cd 8 (BO 3 ) 4 SiO 4 : Metal Cation Inducing the Formation of Isolated [BO 3 ] and [SiO 4 ] Units in Borate Silicate