Abstract:<p>The development of industrial application of water splitting demands simple and effective methods for the preparation of highly efficient electrocatalysts that are inexpensive and robust. Herein, we report a simple activation method to decorate 3D cobalt iron oxyhydroxide (CoFe-OOH) nanosheets on Co<sub>2</sub>P nanoparticles with Ni foams (NF) as substrates. The synthesized catalysts exhibit excellent activity for electrochemical oxygen evolution reaction due to the hierarchical heterostructures and synergistic effects of CoFe-OOH and Co<sub>2</sub>P. The as-prepared catalysts require a low overpotential of 199 mV to deliver 30 mA cm<sup>−2</sup> in oxygen evolution reaction in 1 M KOH with small Tafel slope of 39 mV dec<sup>−1</sup>, indicating favorable kinetics during electrolysis. The synthesized catalysts are further used as cathode and anode for overall water splitting, which only requires a cell voltage of 1.60 V at a current density of 30 mA cm<sup>−2</sup>. This work provides new insights on the preparation of efficient electrocatalysts for overall water splitting, which may have the potentials for industrial water electrolysis.</p>
What problem does this paper attempt to address?
This paper aims to meet the needs of water electrolysis in industrial applications, especially to find simple and effective methods for preparing highly efficient electro - catalysts, which should be low - cost and have stable performance. Specifically, the paper studies the growth of three - dimensional cobalt - iron hydroxyoxide (CoFe - OOH) nanosheets and cobalt phosphide (Co₂P) nanoparticles on a nickel foam (Ni foam, NF) substrate through a simple activation method to achieve an efficient water - splitting reaction.
### Background and Objectives of the Paper
With the intensification of climate change and global warming, it is crucial to find renewable and clean energy resources. Water electrolysis, namely the oxygen evolution reaction (OER) and the hydrogen evolution reaction (HER), has received extensive attention in recent years because they play an important role in hydrogen energy production. However, these two half - electrochemical reactions are usually kinetically slow, resulting in significant electrode overpotentials. Therefore, it is necessary to design efficient electro - catalysts to improve energy efficiency.
Currently, electro - catalysts based on precious metals such as iridium (Ir), ruthenium (Ru) and platinum (Pt) can achieve water splitting with low overpotentials, but the scarcity and high cost of these precious metals limit their wide application. Therefore, researchers are committed to finding alternative materials, such as oxides, sulfides, phosphides, borides and hydroxides, etc. Among them, transition metal compounds, such as nickel, iron, cobalt and copper, have been reported as efficient HER and OER catalysts.
### Research Contents
This paper proposes a simple and efficient activation method to grow cobalt - iron hydroxyoxide nanosheets and cobalt phosphide nanoparticles on a nickel foam substrate. The catalysts prepared by this method exhibit excellent OER and HER activities and stabilities under alkaline conditions. Specifically:
- **Catalyst Structure**: The catalyst consists of a 3D free - standing hierarchical structure, including CoFe - OOH nanosheets and Co₂P nanoparticles.
- **Catalytic Performance**: The synthesized catalyst only needs an overpotential of 199 mV to reach a current density of 30 mA cm⁻² in OER, and the Tafel slope is 39 mV dec⁻¹, indicating good kinetic performance during the electrolysis process. In addition, these catalysts are also used for overall water splitting, and only a cell voltage of 1.60 V is required to reach a current density of 30 mA cm⁻².
- **Stability**: The catalyst exhibits excellent long - term stability at high current densities. For example, in an OER test at 1.43 V for 70 hours, the current density hardly decreases.
### Conclusions
In summary, this paper has developed a simple strategy to assemble a 3D free - standing hierarchical CoFe - OOH@Co₂P/NF heterostructure catalyst for overall water splitting through an activation method. Due to the synergistic effect and hierarchical structure, this catalyst provides more active sites and improves the activity of the sample. The prepared catalyst exhibits excellent OER activity and long - term stability in alkaline solutions, showing great potential in overall water splitting. This work provides a new strategy for synthesizing overall water - splitting catalysts by constructing the interaction between electro - catalytic OER and HER catalysts.