Dual Crosslinked PMMA/BaTiO3 Polymer Nanocomposite Dielectrics for Flexible Film Capacitors

Kun Zhang,Xiaoya Hou,Lei Liu,Jie Zhang,Yu Lei Zhang
DOI: https://doi.org/10.1039/d2nj05673a
IF: 3.3
2022-12-28
New Journal of Chemistry
Abstract:The BaTiO3(BT) nanoparticles were surface modified by polyethylene glycol methacrylate phosphate, and the C=C groups on the phosphate were used as the reaction sites with methyl methacrylate (MMA) monomers for in-situ polymerization. PMMA-BT polymer nanocomposites were prepared for flexible film capacitors application. The prepared nanocomposites could be dissolved in DMF as colorless and transparent solutions. The surface modification of BT nanoparticles, in-situ polymerization, and the thermal crosslinking structure of PMMA-BT were confirmed by FTIR, EDS, XRD, and XPS characterizations. Through high-resolution TEM characterization, the BT nanoparticles were completely coated by organic matter to form the polymer nanocomposite with the core-shell structure. Under the surface and cross-section SEM characterization, the polymer nanocomposites films had the advantage of being extremely uniform with the thickness of about 700 nm. The dense and pinhole-free polymer nanocomposite film of PMMA-BT (13 wt%) had a dielectric loss as low as 0.043, and a dielectric constant of 9.55. In term of the performance, the film capacitor had a maximum energy storage density of 8.5 J/m3, and a high dielectric strength of 447 V/μm. In order to further improve the dielectric properties, PMMA-BT nanocomposites with double crosslinked network structure were prepared by adding methylated poly(melamine-co-formaldehyde) solution (PMF) into PMMA-BT. The dielectric loss of the PMMA-BT film after secondary crosslinking was further reduced to 0.031. In addition, the relationship between dielectric properties and the temperature was investigated, and it was found that the polymer nanocomposite films with double-crosslinked network structure had better thermal stability at high temperature.
chemistry, multidisciplinary
What problem does this paper attempt to address?