Aluminum coating of twinning-induced plasticity plates via plasma-enhanced magnetron sputtering as a potential industrial technique

Kaice Zhang,Jinlong Li,Yukun Zhang,Xiaodong Yu,Yanwen Zhou,Peng Gao
DOI: https://doi.org/10.1016/j.surfcoat.2021.126937
IF: 4.865
2021-04-01
Surface and Coatings Technology
Abstract:<p>Challenges are encountered in the use of the conventional hot-dip galvanization process to deposit a protective layer on the surface of twinning-induced plasticity (TWIP) steel due to the low wettability, which is caused by manganese oxidation on the surface of the steel. In a vacuum environment and after conducting etching on the surface to remove surface oxides, corrosion-resistant aluminum (Al) coatings were prepared on the surface of TWIP steel via the hot-wire plasma-enhanced magnetron sputtering (PEMS) technique under various target and wire discharge currents (I <sub>hot-wires</sub>/ I <sub>target</sub>). The substrate ion current density at -50 V was as high as 0.88 mA/cm<sup>2</sup> under a high hot wire discharge current of 20 A and a low target current of 3 A (20 A/3 A), which was 4 times the ion current under I <sub>hot-wires</sub>/ I <sub>target</sub> of 5 A/3 A, respectively. According to an analysis of the coatings via pulsed radio frequency glow discharge optical emission spectroscopy, Al, Fe and Mn elements diffused at the interface between the coating and steel substrate. The diffusion layers on both sides of the interface resulted in the Al coating remaining well adhered to the surface of the TWIP steel after Rockwell indentation, scratch testing and Erichsen cupping tests. As the sacrificial and passivated anode, the self-corrosion potential of the dense Al coating increased from -0.770 V of the TWIP steel to -0.471 V, and the corrosion current decreased from 3.91×10<sup>-4</sup> A/cm<sup>2</sup> to 6.14×10<sup>-5</sup> A/cm<sup>2</sup>. The dense coating remained undamaged after electrochemical corrosion. Additionally, the structure of the TWIP steel was not affected by the PEMS coating processes.</p>
physics, applied,materials science, coatings & films
What problem does this paper attempt to address?
The problem that this paper attempts to solve is the challenges faced in depositing anti - corrosion aluminum (Al) coatings on the surface of twinning - induced plasticity (TWIP) steel plates by plasma - enhanced magnetron sputtering (PEMS) technology. Specifically, the traditional hot - dip galvanizing process encounters the problem of low wettability when depositing a protective layer on the TWIP steel surface, which is mainly caused by manganese oxidation on the steel surface. The paper proposes a method of preparing anti - corrosion aluminum coatings using hot - wire plasma - enhanced magnetron sputtering technology after etching to remove surface oxides on the TWIP steel surface in a vacuum environment. This method aims to overcome the problems encountered in the traditional hot - dip galvanizing process, improve the corrosion resistance of TWIP steel, and ensure good adhesion between the coating and the substrate. The paper explores in detail the effects of different target currents and hot - wire discharge currents (\(I_{\text{hot - wires}}/I_{\text{target}}\)) on the substrate current density, structure, adhesion, and anti - corrosion performance. It is found that under the conditions of high hot - wire discharge current (20 A) and low target current (3 A), the aluminum coating has the highest density, the strongest adhesion, and good anti - corrosion performance. In addition, through pulsed radio - frequency glow - discharge optical emission spectroscopy analysis, the element diffusion at the interface between the coating and the steel substrate was studied, and it was found that Fe, Mn, and Al elements form a diffusion layer on both sides of the interface, which is helpful for good adhesion between the coating and the substrate. Overall, by optimizing the PEMS process parameters, this paper has successfully solved the key problems in the preparation of anti - corrosion coatings on the TWIP steel surface, providing an effective solution for industrial applications.