Abstract:In the present study, we pyrolyzed a waste tire at various temperatures under an N 2 atmosphere and a water environment in an autoclave reactor to investigate the effect of water on tire degradation. The analysis involved a comparison of product distribution, char properties, oil composition, and the behavior of heteroatom elements (especially oxygen, nitrogen, and sulfur) under different atmospheres. Elemental analysis, functional-group identification, and chemical state analysis of sulfur were performed for chars. In addition, the chemical composition, elemental composition, and molecular weight of the produced oils were evaluated. The heavy fraction of oils, not detectable by gas chromatography-mass spectrometry (GC-MS), was analyzed through Fourier-transform ion cyclotron resonance mass spectrometry (FT-ICR MS). The findings revealed that high temperatures promoted oil cracking, resulting in the formation of light oils in both pyrolysis and hydrolysis processes. Compared to pyrolysis, hydrolysis generated a higher yield of low molecular–weight oil. Elevated hydrolysis temperatures promoted aromatization, yielding an oil with a low H/C ratio and a high double bond equivalent number. Consequently, the concentration of aromatics in the light fraction of oils generated from the hydrolysis process exceeded that in oils from the pyrolysis process. Temperature exhibited a limited impact on oil composition during the pyrolysis process. Hydrolysis promoted the release of heteroatom-containing compounds at low temperatures. During pyrolysis, nitrogen was gradually released from the solid phase, whereas nitrogen-containing compounds were released early during hydrolysis, with gas-phase nitrogen accounting for more than 50 wt% at 320 °C. A maximum D-limonene yield of 45.58% was obtained at 360 °C within 0 min of hydrolysis, with the potential conversion of D-limonene into aromatics at higher hydrolysis temperatures. These results contribute to the understanding of tire valorization via hydrolysis.

Comparison of the Effect of Kaolin and Bentonite Clay (Raw, Acid-Treated, and Metal-Impregnated) on the Pyrolysis of Waste Tire

Influence of Co-Pyrolysis and Catalysis of Biomass with Waste Tire on Pyrolytic Oil Properties

Impact of Bentonite Clay on In Situ Pyrolysis vs. Hydrothermal Carbonization of Avocado Pit Biomass

Sodium bentonite and kaolin clays: Comparative study on their FT-IR, XRF, and XRD

A comparative study of the pyrolysis and hydrolysis conversion of tire

Catalytic pyrolysis of tire waste: Impacts of biochar catalyst on product evolution

Hydrotreatment of Pyrolysis Oil from Waste Tire in Tetralin for Production of High-Quality Hydrocarbon Rich Fuel

Coke Formation and Zeolite Catalyst Effects on Products from Co‐pyrolysis of Waste Tyre and Poplar Wood in a Semi‐Batch Reactor under N2 Atmosphere

Catalytic pyrolysis of lignite with clay catalyst activated with spent pickling liquor

Kinetic analysis of waste tire pyrolysis with metal oxide and zeolitic catalysts

Study of waste tire pyrolysis in a rotary kiln reactor in a wide range of pyrolysis temperature

From Waste Tire to High Value-Added Chemicals: an Analytical Py-GC/TOF–MS Study

Application of TiO2/Bentonite on the Catalytic Pyrolysis of Oil Sludge

Influence of Pyrolytic Carbon Black Derived from Waste Tires at Varied Temperatures within an Industrial Continuous Rotating Moving Bed System

Properties of Pyrolytic Chars and Activated Carbons Derived from Pilot-Scale Pyrolysis of Used Tires

BTEX recovery from waste rubbers by catalytic pyrolysis over Zn loaded tire derived char

Pilot-Scale Pyrolysis of Scrap Tires in A Continuous Rotary Kiln Reactor

Dynamic Pyrolysis Characteristics, Kinetics and Products Analysis of Waste Tire Catalytic Pyrolysis with Ni/Fe-ZSM-5 Catalysts Using TG-IR-GC/MS

Alkaline Earth Metal-Based Minerals/wastes-Catalyzed Pyrolysis of Poly(ethylene Terephthalate)/poly(butylene Terephthalate) for Benzenes-Enriched Oil Production

Catalytic Degradation of High-Density Polyethylene over A Clay Catalyst Compared with Other Catalysts

Production of Composite Sorption-Active Materials Based on Carbon Black and Clay Material from Man-Made Waste