Crystallization and luminescence properties of Er/Yb-doped glass-ceramics based on A 2 O-ZnO-SiO 2 system (A = Li, Na, K, Cs)

Petr Vařák,Jan Baborák,Emmanuel Véron,Alena Michalcová,Jakub Volf,Mathieu Allix,Pavla Nekvindová

DOI: https://doi.org/10.1016/j.jnoncrysol.2023.122783

IF: 4.458

2024-01-01

Journal of Non-Crystalline Solids

Abstract:Er/Yb-doped glass-ceramics from the A 2 O-ZnO-SiO 2 system (A = Li, Na, K, Cs) were prepared. The glass-ceramics contained different crystalline phases, including zinc oxide ZnO, zinc silicate Zn 2 SiO 4 (willemite) or alkali zinc silicates A 2 ZnSiO 4 . The tendency to crystallize was shown to increase with decreasing radius of the alkali ions, from Cs + to Li + . The Na 2 O-ZnO-SiO 2 system was found to be favorable for the crystallization of the rhombohedral modification of Zn 2 SiO 4 (willemite) while the K 2 O-ZnO-SiO 2 system was shown to contain the largest amount of ZnO (zincite). The high crystallinity of the samples caused by annealing the samples to temperatures above 800 °C resulted in a significant increase in the emission intensity around 1.5 μm, a change in the shape of the luminescence band and an increase in the emission lifetime at 1.5 μm from a value cca 10 ms up to a 15 ms.

materials science, multidisciplinary, ceramics