Abstract:CuCrZr has good conductivity , thermal conductivity and high strength and is widely used in the production of continuous casting mold. In this study, for the first time, high-performance CuCrZr coatings were successfully deposited on the surface of CuCrZr mold by laser assisted cold spray (LACS) method as a preliminary trial to validate LACS a repair technique of worn mold surfaces. This study systematically characterizes the microstructure, microhardness, bonding strength, electrical conductivity, wear performance, and thermal shock performance of CS, concentric LACS and eccentric LACS coatings. The results show that compared to CS, LACS shows great improvements in coating density, bond strength, friction and wear performance, and electrical conductivity, thus exhibiting significant prospects in the repair of mold. In particular, eccentric LACS CuCrZr coatings feature higher bonding strength and deposition efficiency, while concentric LACS coatings have better wear, hardness, and electrical conductivity. The best overall coating performance is achieved at eccentric LACS-4 kW-5.5 mm CuCrZr coating which exhibits a porosity of 0.49 %, a grain size of 1.06 μm, a microhardness of 200 HV 0.3 , a bond strength of 205 MPa (on CuCrZr substrates), a friction coefficient of 0.48 and a wear rate of 1.55 × 10 -5 mm 3 /N·m (counterbody: GCr15 balls, 15 N load), an electrical conductivity of 63.50 % IACS, and a thermal shock resistance of > 120 cycles under 650 °C. The mechanisms associated with microstructural formation and mechanical performances of LACS coatings are also analyzed. There was no obvious phase change within the coating, while a heat affected zone is formed at the coating-substrate interface with the formation of Cu x Zr y phases and slight oxides. The grain characteristics of LACS coatings include deformed grains, recovered grains, recrystallized grains. The wear mechanisms of LACS coatings are combined adhesive wear and abrasive wear.

Evaluation of cold-sprayed CuCr coatings as contact materials for vacuum interrupters

Investigation of vacuum arc ignition characteristics and erosion morphology microstructure characteristics of CuCr55 electrode contact materials

Review of the recent Chinese research on the electrical properties of CuCr contacts for vacuum interrupters

Arc erosion resistance of WC/CuCr30 composites based on changing of Cr particle morphology and orientation

Thermal and arc erosion behavior of CuCr contact material based on large plastic deformation treatment

Microstructure, mechanical properties, and tribological properties of laser assisted cold sprayed CuCrZr coatings: Influences of laser power and laser position

Study on Microstructure and Properties of Cr3C2/Fe Coating Prepared by Arc Spraying on Copper Surface

Tribological Behavior of Atmospheric Plasma-Sprayed Cu-Ni Coatings

Deposition of NiCrBSi coatings by atmospheric plasma spraying and dry-ice blasting: Microstructure and wear resistance

Comparative Study of Thermally Sprayed Coatings Under Different Types of Wear Conditions for Hard Chromium Replacement

Microstructure and mechanical performance of cold spray Cr coatings

Microstructure, mechanical properties, and cavitation erosion performances of cold sprayed CuZn35 coatings

Effect of Particle Incident Angle on the Hardness and Thermal Conductivity of Cu Coating Applied to a Cr-Zr-Cu Substrate using High-Pressure Cold Spray

Performance in Resistance to Surface Fatigue for Cr 3 C 2 –25%NiCr Coatings by Plasma Spray and CDS Spray

Effects of Different Post-Treatments on Arc Erosion Resistance of Cold-Sprayed AgC Composite Electric Contact

Microstructure, property and high-temperature wear performance of Cr 3 C 2 -based coatings deposited by conventional and ID-HVAF spray torches: A comparative study

Analysis of Erosion Resistance of CuC Arcing Contacts Manufactured by Plasma Spraying Technology

Influence of WC particles addition on material transfer behavior of CuCr30 contact material

Comparative Study on the Cavitation Erosion and Sliding Wear of Cold-Sprayed Al/Al2O3 and Cu/Al2O3 Coatings, and Stainless Steel, Aluminium Alloy, Copper and Brass

Ti–Cu Coatings Deposited by a Combination of HiPIMS and DC Magnetron Sputtering: The Role of Vacuum Annealing on Cu Diffusion, Microstructure, and Corrosion Resistance

Cr and Mo Cathode Spots Distribution Characteristics with External Axial Magnetic Field