Porous Plate-like MoP Assembly as an Efficient pH-Universal Hydrogen Evolution Electrocatalyst
Yanqing Jiao,Haijing Yan,Ruihong Wang,Xiuwen Wang,Xiaomeng Zhang,Aiping Wu,Chungui Tian,Baojiang Jiang,Honggang Fu
DOI: https://doi.org/10.1021/acsami.0c13533
2020-10-22
Abstract:Molybdenum phosphide is one of the most potential electrocatalysts for the hydrogen evolution reaction (HER), whereas it is still challenging to achieve an efficient molybdenum phosphide-based catalyst that performs well over a wide pH range. Herein, a porous nanoplate composed of small MoP flakes confined in thin N, P, S-triple-doped carbon () was prepared by the assembly of phosphomolybdic acid (H<sub>3</sub>PMo<sub>12</sub>O<sub>40</sub>·<i>n</i>H<sub>2</sub>O, {PMo<sub>12</sub>}) and egg white, followed by phosphorization. Given its small size (ca. 1 nm) in favor of deriving small particles and the oxygen-rich surface with strong coordination ability, the {PMo<sub>12</sub>} cluster was selected to combine with egg white to obtain a lamellar hybrid precursor via a hydrogen bond. Through controllable phosphating, a nanoplate organized by interconnected MoP particles was generated, accompanied by the in situ formation of the N, P, S-doped carbon thin layer and pores from the pyrolysis of egg white. The plentiful pores, thin carbon coating, and multielement doping bring about promoted electrolyte/bubble diffusion, enhanced conductivity and stability, and lowered adsorption energy of hydrogen/hydroxyl, respectively. All of the above merits endow with prominent activity with low overpotentials of 50, 76, and 71 mV at 10 mA cm<sup>–2</sup> toward the HER in alkaline, neutral, and acid media, respectively, and nearly no attenuation after 40 h of testing. Especially, compared with commercial Pt/C, exhibits similar low onset potential and even better at large current density in 1 M KOH. The electrolyzer equipped with the cathode and the NiFe-LDH anode requires only 1.52 V to deliver 10 mA cm<sup>–2</sup> and can be powered by a solar cell (1.524 V) charged by sunlight.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c13533?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c13533</a>.Simulated solar power assisted water splitting with gas bubbles generation at the electrode surface (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c13533/suppl_file/am0c13533_si_001.mp4">MP4</a>)Experimental section, IR spectra, XRD patterns, SEM images, TEM images, AFM images, TG curves, Raman spectra, nitrogen adsorption/desorption isotherms, WF drawings, polarization curves, exchange current density, <i>C</i><sub>dl</sub> measurements, and comparison tables of recently reported HER electrocatalysts in alkaline, neutral, and acid media (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c13533/suppl_file/am0c13533_si_002.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology