Abstract:Clusters appear in the prenucleation stage of QDs. They are relatively transparent in optical absorption and are the precursor compounds (PCs) of MSCs. For one CdSe prenucleation‐stage sample, CdSe MSC‐390 transforms to MSC‐415; mixed with one CdS prenucleation‐stage sample, CdSeS MSCs are seen. The PC‐to‐PC transformation is assisted by monomer substitution. With enough CdS monomers, the CdSe PC can transform almost entirely to the CdS PC. The synthetic application of prenucleation‐stage samples of colloidal semiconductor quantum dots (QDs) is in its infancy. It is shown that when two prenucleation‐stage samples of binary CdSe and CdS are mixed, ternary CdSeS magic‐size clusters (MSCs) grow at room temperature in dispersion. As the amount of the CdS sample increases, the optical absorption of the CdSeS MSCs blueshifts from ≈380 to ≈360 nm. It is proposed that the cluster in the CdSe sample reacts with the CdS monomer from the CdS sample. The monomer substitution reaction of CdSe by CdS can proceed continuously; thus, CdSeS MSCs with tunable compositions are obtained. The present study provides compelling evidence that clusters formed in the prenucleation stage of QDs. The clusters are precursor compounds (PCs) of MSCs, transforming at room temperature with the thermoneutrality principle of isodesmic reactions. The nucleation and growth of QDs follows a multi‐step non‐classical instead of one‐step classical nucleation model.

Lower-Temperature Nucleation and Growth of Colloidal CdTe Quantum Dots Enabled by Prenucleation Clusters with Cd-Te Bond Conservation

CdTe/CdS、CdTe/ZnS核壳结构半导体量子点制备及荧光特性

Aqueous synthesis of highly monodispersed thiol-capped CdTe quantum dots through electrochemical approach.

Understanding the Growth Mechanism of HgTe Colloidal Quantum Dots through Bilateral Injection

Preparation and Optical Properties of Core/Shell Type-II CdxZn1-xTe/CdS Quantum Dots

Synthesis and Characterization of Monodisperse CdSe Quantum Dots with Zinc Blende Structure

Aqueous Synthesis of Highly Luminescent CdTe Quantum Dots and Its Growth Mechanism

Size- and Shape-Controlled Synthesis of CdTe and PbTe Nanocrystals Using Tellurium Dioxide as the Tellurium Precursor

Strategy for Performance Enhancement of Cd1-XZnXTe/CdS Core/shell Quantum Dot Sensitized Solar Cells Through Band Adjustment

Intensification of Nucleation Stage for Synthesizing High Quality CdSe Quantum Dots by Using Preheated Precursors in Microfluidic Devices

Simple Synthesis of Highly Luminescent Water-Soluble CdTe Quantum Dots with Controllable Surface Functionality

The Design of Mn2+&Co2+ Co-Doped CdTe Quantum Dot Sensitized Solar Cells with Much Higher Efficiency.

Rapid Aqueous Synthesis of High-quality CdTe Colloidal Quantum Dots

Preparation and Characterization of Highly Luminescent Water-Soluble CdTe Quantum Dots As Optical Temperature Probes.

Room-Temperature Evolution of Ternary CdTeS Magic-Size Clusters Exhibiting Sharp Absorption Peaking at 381 nm

Pathway of Room‐Temperature Formation of CdSeS Magic‐Size Clusters from Mixtures of CdSe and CdS Samples

An Improved One-Pot Aqueous Phase Synthesis Of Cdte Qds

A Novel Two-Step Controlled Basic Water Phase Method for Synthesizing Size-Tunable CdTe/Cd(OH)2 Core/shell Quantum Dots with High Quantum Yield and Excellent Stability

Temperature-dependent Photoluminescence of Highly Luminescent Water-Soluble CdTe Quantum Dots

Preparation of water-soluble CdTe/CdS core/shell quantum dots with enhanced photostability

Synthesis of Type-I CdTe Core and Type-II CdTe/CdS Core/Shell Quantum Dots by a Hydrothermal Method and Their Optical Properties