Abstract:Objective: To evaluate the influence of antioxidants (ATX) resveratrol, winter's bark, green tea and yerba mate on the bond strength between bleached enamel and the nanohybrid composite resin. Methodology: Bovine incisor crowns (n=132) were randomly divided into 22 groups (n=6) according to the application times (5, 10, 15, 30, and 60 minutes) of each antioxidant. Teeth restored without previous bleaching or ATX constituted the non-bleached control group (NB Ctrl) (n=6), and teeth restored after bleaching and without ATX represented the bleached control group (B Ctrl) (n=6). The 35% hydrogen peroxide was applied for 45 minutes (3 application of 15 min) to the buccal enamel surface. ATX was used after bleaching for the specified time of each group and removed with air-water spray. The enamel was etched with 37% phosphoric acid (30 seconds) and rinsed with air-water spray. The adhesive resin was applied to the enamel dry surface. Teeth were restored using 1mm composite resin increments (10 × 10 × 3 mm) and sectioned in test specimens of 6 mm in length and 1 mm 2 in cross-sectional area submitted to microtensile bond strength test (0.5 mm/min). The load (N) at failure was recorded, and the bond strength (σt) was calculated (MPa). The fracture area was analyzed under optical microscopy, and failures were classified as cohesive, mixed, or adhesive. Data was evaluated by Kruskal-Wallis and Dunn tests (p≤0.05). Results: B Ctrl group presented lower σt than NB Ctrl (p<0.001). Applying resveratrol for 5 or 10 minutes, winter's bark for 10 or 15 minutes, green tea for less than 15 minutes, and yerba mate for 15 minutes provided similar σt between bleached enamel and nanohybrid composite to the control group. Conclusion: Restorative procedures performed immediately after tooth bleaching compromises adhesion. Experimental antioxidants applied to bleached enamel can increase the immediate bond strength of restorations performed directly after bleaching, with similar values to those observed in unbleached enamel.

Effect of antioxidants on adhesive bond strength to bleached enamel