Two-Dimensional Covalent Organic Frameworks with Cobalt(II)-Phthalocyanine Sites for Efficient Electrocatalytic Carbon Dioxide Reduction
Bin Han,Xu Ding,Baoqiu Yu,Hui Wu,Wei Zhou,Wenping Liu,Chuangyu Wei,Baotong Chen,Dongdong Qi,Hailong Wang,Kang Wang,Yanli Chen,Banglin Chen,Jianzhuang Jiang
DOI: https://doi.org/10.1021/jacs.1c02145
IF: 15
2021-05-03
Journal of the American Chemical Society
Abstract:The rapid development in synthesis methodology and applications for covalent organic frameworks (COFs) has been witnessed in recent years. However, the synthesis of highly stable functional COFs still remains a great challenge. Herein two-dimensional polyimide-linked phthalocyanine COFs (denoted as CoPc-PI-COF-1 and CoPc-PI-COF-2) have been devised and prepared through the solvothermal reaction of the tetraanhydrides of 2,3,9,10,16,17,23,24-octacarboxyphthalocyaninato cobalt(II) with 1,4-phenylenediamine and 4,4′-biphenyldiamine, respectively. The resultant CoPc-PI-COFs with a four-connected sql net exhibit AA stacking configurations according to powder X-ray diffraction studies, showing permanent porosity, thermal stability above 300 °C, and excellent resistance to a 12 M HCl aqueous solution for 20 days. Current–voltage curves reveal the conductivity of CoPc-PI-COF-1 and CoPc-PI-COF-2 with the value of 3.7 × 10<sup>–3</sup> and 1.6 × 10<sup>–3</sup> S m<sup>–1</sup>, respectively. Due to the same Co(II) electroactive sites together with similar permanent porosity and CO<sub>2</sub> adsorption capacity for CoPc-PI-COFs, the cathodes made up of COFs and carbon black display a similar CO<sub>2</sub>-to-CO Faradaic efficiency of 87–97% at applied potentials between −0.60 and −0.90 V (vs RHE) in 0.5 M KHCO<sub>3</sub> solution. However, in comparison with the CoPc-PI-COF-2&carbon black electrode, the CoPc-PI-COF-1 counterpart provides a larger current density (<i>j</i><sub>CO</sub>) of −21.2 mA cm<sup>–2</sup> at −0.90 V associated with its higher conductivity. This cathode also has a high turnover number and turnover frequency, amounting to 277 000 and 2.2 s<sup>–1</sup> at −0.70 V during 40 h of measurement. The present result clearly discloses the great potential of 2D porous crystalline solids in electrocatalysis.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/jacs.1c02145?goto=supporting-info">https://pubs.acs.org/doi/10.1021/jacs.1c02145</a>.Experimental and theoretical calculation details, PXRD patterns, TGA curves, XPS spectra, XANES spectra, CO<sub>2</sub> sorption curves, and electrocatalytic performance of CoPc-PI-COF-1 and CoPc-PI-COF-2 (<a class="ext-link" href="/doi/suppl/10.1021/jacs.1c02145/suppl_file/ja1c02145_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary