Abstract:An electrocatalytic nitrogen reduction reaction is considered a potential approach for green ammonia production─a zero-carbon fertilizer, fuel, and energy storage for renewable energy. To harness the synergistic properties of perovskites, the inherent dipole moment due to their non-centrosymmetric structure (that facilitates better charge separation), oxygen vacancies, and the presence of Ni metal sites that permit activation and reduction of N2 efficiently, the NiTiO3-based nanoelectrocatalysts have been synthesized. Further, these catalysts have been modified with ultra-small metal nanocrystal co-catalysts to form heterointerfaces that not only aid to improve the charge separation but also activate N2 and lower overpotential requirements. The appearance of peaks corresponding to (012), (104), (110), (11-3), (024), (11-6), (018), (027), and (300) confirms the formation of rhombohedral NiTiO3. The shift in the XRD peak corresponding to the (104) plane to a smaller 2θ value and peak shifting and widening of Raman spectra imply the lattice distortion that signifies the formation of Pd-NiTiO3 and Pt-NiTiO3 heterojunction electrocatalysts with the loadings of 0.4 and 0.3 wt % of Pd and Pt, respectively, as confirmed by ICP-OES analysis. The detailed XPS analysis reveals the presence of Pd (0), Pd (II), and Pt (0), Pt (II) in respective electrocatalysts. The appearance of XPS peaks at 528.7 and 531.1 eV suggests the presence of oxidative oxygen species (O2-/O-) and the presence of oxygen defects due to oxygen vacancy. The detailed nitrogen reduction (NRR) investigation exhibits a 5-fold enhancement in ammonia yield rate (∼14.28 μg h-1 mg-1 at -0.003 V vs RHE), a faradic efficiency of 27% (at 0.097 V vs RHE) for Pd-NiTiO3 electrocatalysts than that for bare NiTiO3 (3.08 μg h-1 mg-1), and 9-folds higher than that of the activity shown by the commercial TiO2 (P25) (1.52 μg h-1mg-1). The formation of ammonia was further confirmed by using isotopic nitrogen as the feeding gas. Furthermore, the highest NRR is observed at lower cathodic potential (-0.003 V vs RHE) in the case of the Pd-NiTiO3 electrocatalyst than that of the Pt-NiTiO3 electrocatalyst (-0.203 V vs RHE), implying significantly reduced overpotential requirement. Such enhanced NRR activity with lower overpotential requirement in the case of the Pd-NiTiO3 electrocatalyst is due to efficient charge separation as shown by the semicircle Nyquist plot, decreased photoluminescence emission intensity, shorter average lifetime (∼29 ns) of excitons, appropriate band bending, and improved activation of N2 by the oxygen vacancies and heterointerface formed between Pd nanocrystals and NiTiO3. Furthermore, no change is observed in the current density, after stabilization in the initial few seconds, even up to 2 h, which signifies that these electrocatalysts are stable. The structural and morphological integrity of the optimized catalyst remained even after the nitrogen reduction reactions, as revealed by no significant change observed in FESEM, elemental mapping, and EDS analysis.

Modulating the Active Sites of Oxygen‐Deficient TiO 2 by Copper Loading for Enhanced Electrocatalytic Nitrogen Reduction to Ammonia

Modulation of surface properties on cobalt phosphide for high-performance ambient ammonia electrosynthesis

In Situ Loading of Cu2O Active Sites on Island-like Copper for Efficient Electrochemical Reduction of Nitrate to Ammonia.

Modulation of Charge Distribution Enabling CuNi Nano-Alloys for Efficient Ammonia Oxidation Reaction to Nitrite Production

Boosting charge-transfer in tuned Au nanoparticles on defect-rich TiO 2 nanosheets for enhancing nitrogen electroreduction to ammonia production

Enhanced Nitrogen Reduction to Ammonia by Surface- and Defect-Engineered Co-catalyst-Modified Perovskite Catalysts under Ambient Conditions and Their Charge Carrier Dynamics

Cu/CuOx In-Plane Heterostructured Nanosheet Arrays with Rich Oxygen Vacancies Enhance Nitrate Electroreduction to Ammonia.

Modulating Oxygen Vacancies of TiO2 Nanospheres by Mn-Doping to Boost Electrocatalytic N2 Reduction

Optimizing Oxidation State of Octahedral Copper for Boosting Electroreduction Nitrate to Ammonia

Ti 2 O 3 Nanoparticles with Ti 3+ Sites toward Efficient NH 3 Electrosynthesis under Ambient Conditions

Nanoporous Nickel–Molybdenum Oxide with an Oxygen Vacancy for Electrocatalytic Nitrogen Fixation under Ambient Conditions

Enhanced localized electron density from PdCu nanoparticles loading on defective TiO2 support for selective nitrate electroreduction to ammonia

Enhancing Localized Electron Density over Pd1.4Cu Decorated Oxygen Defective TiO2-x Nanoarray for Electrocatalytic Nitrite Reduction to Ammonia

Modulating Oxygen Vacancies of TiO 2 Nanospheres by Mn-Doping to Boost Electrocatalytic N 2 Reduction

Mesoporous MnO2 nanosheets for efficient electrocatalytic nitrogen reduction via high spin polarization induced by oxygen vacancy

Introducing oxygen vacancies in a bi-metal oxide nanosphere for promoting electrocatalytic nitrogen reduction

Atomically Dispersed High-Active Site Density Copper Electrocatalyst for the Reduction of Oxygen

Boosting nitrogen electrocatalytic fixation by three-dimensional TiO2−δNδ nanowire arrays

Modulating Nitrogen Adsorption Mode and Microenvironment of Active Sites for Boosting Electrochemical Nitrogen Reduction

Electrocatalytic ammonia synthesis catalyzed by mesoporous nickel oxide nanosheets loaded with Pt nanoparticles

High-Performance Electrocatalytic Conversion of N-2 to NH3 Using Oxygen-Vacancy-Rich TiO2 in Situ Grown on Ti3C2Tx MXene