Abstract:Because of their low density and high specific strength, Mg alloys are considered promising lightweight alloys for various applications. However, due to the high electrochemical activity and poor corrosion resistance, surface modifications of Mg alloys are needed to increase the service life. Hence, an active layered double hydroxides (LDHs) coating was investigated in this study. Owing to the brucite-like layered structure, the weakly bonded interlayer anions can be easily exchanged with other anions in the environment. With the unique anion-exchange mechanism, LDHs coating provides dual protection to the Mg alloy substrate. It can not only act as a physical barrier but also absorb aggressive anions such as Cl - and release corrosion inhibitors to the environment. Compared to the commonly used hydrothermal method to fabricate LDHs coating, which requires high temperature and long process time, electrochemical deposition has the advantages of high deposition rates, simple experimental setup, and highly controllable process parameters. Therefore, in this study, a three-electrode electrochemical setup was used to fabricate Zn-Al LDHs coatings on a ZX21 Mg alloy. Moreover, different anions are intercalated into the interlayer galleries of the prepared Zn-Al LDHs coating through post anion-exchange processes. Through electrochemical analysis in a 3.5 wt% NaCl solution, the prepared anion-exchanged electrodeposited Zn-Al LDHs coating improved the corrosion resistance of ZX21 Mg alloy. Electrochemical impedance spectroscopy (EIS) showed that corrosion impedance increases, while potentiodynamic polarization curves revealed that the corrosion current density ( i corr ) of the coated sample was an order of magnitude lower than the ZX21 Mg alloy substrate. Besides the improvement of corrosion resistance, the formation mechanism of Zn-Al LDHs coating by electrodeposition was also investigated by electrochemical analysis and in situ optical microscopic (OM) observations. The corrosion behavior and microstructure of Zn-Al LDHs coating and the roles played by different intercalated anions will be discussed based on electrochemical analysis and microstructure characterizations. Figure 1

Effect of degradable (CaP and ZnO) nanoparticals void-plugging MgFe-LDHs film on the pitting-responsive behaviors of AZ31 magnesium alloy

Preparing Ca-P Coating on Biodegradable Magnesium Alloy by Hydrothermal Method: in Vitro Degradation Behavior

Enhanced corrosion protection of magnesium alloy via in situ Mg–Al LDH coating modified by core–shell structured Zn–Al LDH@ZIF-8

The effect of surface structure on hydrophobicity and corrosion resistance of the MgAlCe-LDH film prepared on the micro-arc oxidation coating of magnesium alloy

Enhancement of corrosion resistance of AZ31 Mg alloys by one-step in situ synthesis of ZnAl-LDH films intercalated with organic anions (ASP, La)

Effect of solution pH value on the corrosion resistance of Co-Fe LDHs coating developed on MAO treated magnesium alloy AZ31

Preparation of phosphate ion-doped Zn–Fe-layered double hydroxide with corrosion resistance and inducing Ca–P deposition on AZ31 Mg alloy

Corrosion protection properties of different inhibitors containing PEO/LDHs composite coating on magnesium alloy AZ31

In vitro degradation and cytocompatibility of a low temperature in-situ grown self-healing Mg-Al LDH coating on MAO-coated magnesium alloy AZ31

Enhanced Corrosion Resistance of Layered Double Hydroxide Films on Mg Alloy: The Key Role of Cationic Surfactant

Insight into chelating agent stimulated in-situ growth of MgAl-LDH films on magnesium alloy AZ31: The effect of initial cationic concentrations

Self-healing PEO/MgAlLa LDHs-MXene composite coating loaded with 4-aminophenol for corrosion protection of Mg-Gd-Y-Zn LPSO Mg alloy

Corrosion inhibitors for corrosion resistance and self-healing of PEO/MgAlLa layered double hydroxides coating on Mg-Gd-Y-Zn alloy

Influence of Mg substrate on the formation mechanism and corrosion resistance of LDH films

Facile Fabrication and Properties of Super-hydrophobic MgAl-LDH Films With Excellent Corrosion Resistance on AZ31 Magnesium Alloy

Comparison of corrosion resistance of MgAl-LDH and ZnAl-LDH films intercalated with organic anions ASP on AZ31 Mg alloys

Superhydrophobic and smart MgAl-LDH anti-corrosion coating on AZ31 Mg surface

Enhanced corrosion resistance and cytocompatibility of biodegradable Mg alloys by introduction of Mg(OH)2 particles into poly (L-lactic acid) coating

Corrosion Protection Behavior of Aluminate Ion-Loaded Layered Double Hydroxide Coating on AZ31 Magnesium Alloy

Fabrication of Anion-Exchanged Electrodeposited Zn-Al Layered Double Hydroxides (LDHs) Coating on ZX21 Mg Alloy

Intercalation of Y in Mg-Al layered double hydroxide films on anodized AZ31 and Mg-Y alloys to influence corrosion protective performance