Abstract:The magmatic diagenetic environment was simulated by high-temperature melting and natural cooling. A series of glass-ceramics with different Nd2O3 contents were prepared by using complex component granite (aluminosilicate material). The phase evolution of the matrix at different temperatures was studied by X-ray diffraction (XRD). The structure of glass-ceramics was analyzed by infrared spectroscopy (IR) and scanning electron microscopy (SEM). The mechanical properties of glass-ceramics were also evaluated. The results showed that the glass transition of pure matrix begins at 1200 degrees C, and the sample with the highest degree of vitrification is obtained at 1500(degrees)C. The addition of Nd2O3 promoted the melting of Fe3O4 crystal, resulting in the complete amorphous matrix when the Nd2O3 amount is in the range of 20-26 wt.%. With the further increase of Nd2O3 content, Nd-bearing feldspar first appeared. No raw material Nd2O3 was found, indicating that the formation of Nd-bearing feldspar may increase the carrying capacity of the material. The Gaussian fitting results showed that the glass-ceramic samples with Nd2O3 content of 29 wt.% are mainly composed of Q(2) and Q(3) structural units. In the EDS result, part of neodymium was clustered with small bright spots, while the spots were uniformly distributed on the sample surface as a whole. Meanwhile, the addition of Nd2O3 increased the mechanical properties of the samples (3.20 g/cm(3), 8.33 GPa for the sample with 29 wt.% of Nd2O3). The results provide a strategy for the treatment of solid waste with radioactive residual actinides.

The effect of alpha irradiation on the performance of glass matrix in simulated radioactive contaminated soil by microwave treatment

Effect of alpha-particle irradiation on microwave-sintered actinide-contaminated soil glass waste

Effect of irradiation on the phase evolution and chemical stability of neodymium and cerium co-doped simulated radioactive contaminated soil

Crystallization Behavior of Uranium Glass-Ceramic Matrix under Simulated Self-Irradiation Conditions

Microwave sintering for rapid treatment of simulated Nd3+ and Sr2+ radioactive contaminated soil: exploring the influence of Nd:Sr mass ratio and mechanism

Response of Simulated An3+/An4+ Radioactive Soil Vitrification under Alpha-Particle Irradiation

Mechanical and leaching properties of neodymium‐contaminated soil glass‐ceramics

Effect of varying Nd<sub>2</sub>O<sub>3</sub> contents on the structure and mechanical properties of the radioactive waste form: aluminosilicate glass-ceramics

Effect of Soil Elements (si, Al, and Ca) on the Performance and Structure of Simulated An3+ Radioactive Contaminated Soil by Microwave Sintering

Heavy-ion irradiation effects on uranium-contaminated soil for nuclear waste

Rapidly immobilization of simulated An3+ radioactive contaminated soil as glass-ceramics by microwave sintering

Microwave vitrification of simulated radioactively contaminated soil: Mechanism and performance

Microwave Vitrification of Sr-contaminated Soil: Microstructure, Mechanical Properties and Chemical Durability

Rapid solidification of simulated radioactive contaminated soil by continuous microwave sintering: Effects of temperature and doping level

Influence of radiation on borosilicate glass leaching behaviors

Immobilization of Uranium-Contaminated Soil into Glass Waste by Microwave Sintering: Experimental and Theoretical Study

Radiation Stability of a Cementation Matrix for Spent Radioactive Resin

Xe 20+ irradiation effects on soil holding simulated An 4+ waste

Effect of Mass Fraction of CeO2 on Structure of Zirconolite-based Glass-ceramics

Simulated Self-Irradiation Effects of Gd2Ce2O7 Nuclear Waste Form

Heavy-ion Irradiation Effects on Gd2Zr2O7 Ceramics Bearing Complex Nuclear Waste