Rationally designed hierarchical N, P co-doped carbon connected 1T/2H-MoS2 heterostructures with cooperative effect as ultrafast and durable anode materials for efficient sodium storage

Yanli Zhou,Yan Liu,Ming Zhang,Qi Han,Yifei Wang,Xueqin Sun,Xiaoyu Zhang,Caifu Dong,Jianchao Sun,Zikang Tang,Fuyi Jiang

DOI: https://doi.org/10.1016/j.cej.2021.133778

IF: 15.1

2022-04-01

Chemical Engineering Journal

Abstract:MoS2 has attracted great attentions due to the high capacity and layered crystal structure. Whereas the intrinsic poor conductivity and big volume change of common used 2H-MoS2 bring about poor rate capability and bad cycling performance. Herein, three-dimensional N, P co-doped carbon network modified mixed phases of 1T/2H-MoS2 heterostructures (1T/2H-MoS2@PNC) have been rationally fabricated through a facile three-step strategy. Dependent on the cooperate effect of 1T/2H-MoS2 heterostructure and N, P co-doped carbon network, the 1T/2H-MoS2@PNC exhibits a high reversible capacity (475 mAh g−1 at 0.5 A g−1), outstanding rate capability (347 mAh g−1 at 10 A g−1) and long-term cyclic life up to 1000 cycles without capacity loss, obviously superior to 1T/2H-MoS2@PNC with different carbon contents/synthesis temperatures, 2H-MoS2@PNC and 1T/2H-MoS2@NC. Reaction kinetics and theoretical calculation have been investigated to verify the synergetic advantages of 1T/2H-MoS2 and N, P co-doping of carbon networks. Moreover, various ex-situ techniques have been employed to disclose the reaction mechanism of 1T/2H-MoS2@PNC. The assembled Na3V2(PO4)3//1T/2H-MoS2@PNC full batteries also demonstrate good electrochemical properties (a discharge capacity of 216 mAh g−1 over 300 cycles at 0.5 A g−1). All the results manifest the prospective application of 1T/2H-MoS2@PNC as high-performance anode materials for large-scale energy storage.

engineering, chemical, environmental