Mechanical Behavior of Metastable β Ti–10V–2Fe–3Al Alloy with and without Presence of α Phase

Elena Pereloma,Mitchel J. B. Nancarrow,Xiaohui Bian,Ryan Naseri,Qiang Zhu,Lachlan Smillie,Ahmed A. Saleh

DOI: https://doi.org/10.1002/adem.202401931

IF: 3.6

2024-12-13

Advanced Engineering Materials

Abstract:Digital image correlation and electron microscopy studies of uniaxial tensile‐tested metastable β Ti‐10V‐2Fe‐3Al alloy with varied α phase content (0‐20%), revealed an increase in triggering stress for initiation of α′′ martensite formation, decrease in the extent of β →α′′ transformation with an increase in the amount of α phase and no change in the mechanism of plastic deformation accommodation. A combination of digital image correlation during uniaxial tensile testing with electron microscopy characterization of microstructure is used to study the details of mechanical behavior of the Ti–10V–2Fe–3Al (wt%) alloy with α phase amount variation from 0 to 20%. Although the triggering stress for deformation‐induced α′′ martensite formation has increased and the extent of transformation reduced with an increase in α phase fraction, the deformation mechanism has not changed. The α′′ martensite transformation starts from the initiation of single variants of martensite at grain boundaries and/or α/β interfaces in favorably oriented toward deformation axis β grains. It follows by self‐accommodation of strain by α′′ martensite via formation of grids and V‐shaped arrangements of {111}α′′ type I twins at higher tensile strains.

materials science, multidisciplinary