Fouling mitigation of a graphene hydrogel membrane electrode by electrical repulsion and in situ self-cleaning in an electro-membrane reactor

Jingqiu Sun,Chengzhi Hu,Baichun Wu,Jiuhui Qu

DOI: https://doi.org/10.1016/j.cej.2020.124817

IF: 15.1

2020-08-01

Chemical Engineering Journal

Abstract:<p>The conductive membrane can improve water flux and selectivity when it is employed as a membrane electrode. However, stability of the membrane structure during electro-filtration is still a challenge. In this study, a conductive graphene hydrogel membrane (GHM) was fabricated by compaction of a graphene hydrogel under external pressure. The pore size of GHM was stable at ~100 nm under anodic oxidation and cathodic reduction state, which was beneficial for long term electro-control of membrane fouling. When the GHM was negatively charged, membrane fouling was mainly reduced by electrical repulsion, and <em>in situ</em> electro-oxidation played a primary role in the self-cleaning to recover water flux. The water flux of the GHM electrode with a bias of −1 V was 10% higher than that of the GHM without applied bias. After fouled by bovine serum albumin (BSA), the flux recovery ratio of GHM electrode could maximally achieve 99.0 ± 1.4% by the self-cleaning, indicating that almost all the foulants were removed from the GHM. Lower foulant concentration, higher electrolyte concentration, and longer self-cleaning time were beneficial to recover the flux. These findings provide a foundation for the development and application of the electro-membrane reactor (EMR) system using conductive membranes.</p>

engineering, chemical, environmental