Microstructure characterization of plasma electrolytic oxidation coating on Hf-Nb-Ta-Zr high entropy alloy
Hu Chen,Xin Li,Wanhuan Yang,Qian Zhou,Chi Xu,Jiancheng Du,Xiaoyue Jin,Wenbin Xue
DOI: https://doi.org/10.1016/j.matchar.2024.114403
IF: 4.537
2024-09-29
Materials Characterization
Abstract:The morphology, composition, and microstructure of plasma electrolytic oxidation (PEO) coating on Hf-Nb-Ta-Zr high entropy alloy (HEA) were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), Raman spectroscopy, glow discharge optical emission spectroscopy (GDOES) and transmission electron microscopy (TEM). The formation mechanism of PEO coating was analyzed. It was found that a dense PEO coating of ∼4 μm thick on the HEA surface was formed, which consisted of tetragonal and monoclinic ZrO 2 phases, tetragonal and monoclinic HfO 2 phases, Nb 2 O 5 and Ta 2 O 5 phases. The PEO coating from the alloy substrate to the surface contained five distinctive layers: amorphous barrier layer, nanocrystalline layer, columnar grain layer, amorphous outer layer, and top porous layer. Their formation was ascribed to the different cooling rates of the melt in the different depths of the discharge channel across the coating. Meanwhile, the formation of an amorphous barrier layer near the HEA substrate was also related to the mutual migration and diffusion of Hf 4+ , Nb 5+ , Ta 5+ , Zr 4+ and O 2− besides the rapid cooling of melt in the bottom of the discharge channel. The columnar grains of ∼70 nm wide were mainly composed of the monoclinic ZrO 2 and monoclinic HfO 2 phases, but both the amorphous layers enrich the Ta and Nb elements. It was believed that the high-content Ta and Nb in the HEA enhanced the formation of the amorphous layers.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing