Synergistically enhancing CO2-tolerance and oxygen reduction reaction activity of cobalt-free dual-phase cathode for solid oxide fuel cells

Mingze Li,Xinyu Zhao,Huihua Min,Guoliang Yuan,Xifeng Ding
DOI: https://doi.org/10.1016/j.ijhydene.2020.09.090
IF: 7.2
2020-11-01
International Journal of Hydrogen Energy
Abstract:<p>High-performance cathodes with adequate CO<sub>2</sub> tolerance are vital for further development of intermediate-temperature solid oxide fuel cells (IT-SOFCs). However, there is always a trade-off between CO<sub>2</sub> tolerance and oxygen reduction reaction (ORR) performance for single-phase cathodes. Here, we report a cobalt-free Ba<sub>0.6</sub>La<sub>0.4</sub>FeO<sub>3-<em>δ</em></sub>-Ce<sub>0.8</sub>Sm<sub>0.2</sub>O<sub>2-<em>δ</em></sub> (BLF-SDC) dual-phase cathode with excellent ORR activity and CO<sub>2</sub> tolerance. Introducing ionic conductor Ce<sub>0.8</sub>Sm<sub>0.2</sub>O<sub>2-<em>δ</em></sub> (SDC) into the Ba<sub>0.6</sub>La<sub>0.4</sub>FeO<sub>3-<em>δ</em></sub> (BLF) phase can boost ORR activity due to the extended active sites and enhanced oxygen surface exchange process with a polarization resistance of 0.121 Ω cm<sup>2</sup> for the BLF-30% SDC (weight ratio, BLF-30SDC) cathode at 700 °C. The CO<sub>2</sub> resistance of the BLF-30SDC composite cathode outperforms BLF cathode by three times at 600 °C. This stability enhancement is owing to low CO<sub>2</sub> adsorption of SDC, which is confirmed from thermodynamic calculation. This work indicates that dual-phase mixed conductors can be developed as highly active and stable cathodes for IT-SOFCs.</p>
energy & fuels,electrochemistry,chemistry, physical
What problem does this paper attempt to address?