Remarkable Impact of Chain Backbone on the Performance of Poly(norbornene derivatives)-based Anion Exchange Membranes
Xiaowei Sun,Dafu Cao,Min Liu,Bangbang Wang,Dongpo Song,Li Pan,Nanwen Li,Yuesheng Li
DOI: https://doi.org/10.2139/ssrn.4763954
IF: 9.5
2024-05-03
Journal of Membrane Science
Abstract:Chemical stability and the trade-off between ion conductivity and dimensional stability are two primary challenges for the development of suitable anion exchange membranes (AEMs). Herein, a series of non-crosslinked poly(norbornene derivative)-based AEMs containing a bulky steric hindrance hydrophobic arylene substituent were prepared by vinyl addition polymerization (VAP), ring-opening metathesis polymerization (ROMP), and ROMP followed post-hydrogenation, respectively. Compared with ROMP and hydrogenated type membranes, VAP-type membranes, especially the VAP-N-50, exhibited excellent dimensional stability with limited swelling ratio (SR = 27.9%) while higher water uptake (WU = 213.8%) at 80 °C, which is attributed to its rigid VAP-type cyclic chain backbone. Microtopography study demonstrated the existence of nanoscale phase separation in VAP-type AEMs and its association with water uptake and swelling behavior. VAP-N-60 showed excellent hydroxide conductivity up to 105.5 mS cm -1 at 80 °C, while exhibited superior alkaline stability that was not found in ROMP-type membrane ROMP-N-50 and the hydrogenated-type membrane H-ROMP-N-50. After being immersed in 2 M NaOH solution at 80 °C for 1200 h, the hydroxide conductivity loss of VAP-N-60 was only 3.0%. Furthermore, a H 2 /O 2 single cell using VAP-N-50 membrane achieved the highest peak power density of 722 mW cm -2 at 60 °C without back pressure.
engineering, chemical,polymer science