A novel high-sensitivity optical thermometry based on the fluorescence intensity ratio of VO 4 3- to Pr 3+
Yong-Biao Yan,Shuang Li,Shuang-Shuang Ding,Bing-Xue Zhang,Hao Sun,Quan-Hao Ju,Lu Yao,Yan Yongbiao,Li Shuang,Ding Shuangshuang,Zhang Bingxue,Sun Hua,Ju Quanhua,Yao Lu,,
DOI: https://doi.org/10.7498/aps.73.20240012
IF: 0.906
2024-01-01
Acta Physica Sinica
Abstract:It is noteworthy that there has been an exponential increase in the number of scientific papers published and cited on optical thermometry since 2010. Optical thermometry technology is about to witness a significant advancement in terms of sensing, therapy, diagnosis, and imaging. The main focus of current research on optical thermometry is developing high-sensitivity thermometry. In this work, a new thermometry strategy is proposed based on the different temperature-dependent behaviors between the host and the doped ions. Firstly, YVO 4 : x Pr 3+ ( x =0%-1.5%) phosphors were successfully synthesized by the solid-state method. Then, the structure and luminescence properties of the samples were characterized by XRD, SEM and fluorescence spectrophotometer. XRD results showed that Pr 3+ was successfully incorporated into the YVO 4 host, and the samples have a tetragonal phase crystal structure with space group I41/amd. SEM results show that the samples were rectangular-shaped micron particles with smooth surfaces, and the average grain size was about 2.1 μm. Under the excitation of 320 nm, the sample mainly exhibits broadband blue emission around 440 nm and red emission at 606 nm, which are attributed to the charge transfer transition of VO 4 3- and the 1 D 2 → 3 H 4 transition of Pr 3+ , respectively. The relationship between the luminescence of the samples and the concentration of Pr 3+ was studied. It was found that the optimal doping concentration of Pr 3+ was 0.5%, and a higher doping concentration would cause concentration quenching. The reason for concentration quenching is the electric dipole-quadrupole interaction. The luminescence peak positions of the temperature-dependent spectrum of YVO 4 :0.5%Pr 3+ are consistent with those at room temperature. As the temperature increases, the total luminescence intensity gradually decreases, which is caused by thermal quenching, and the mechanism of thermal quenching is analyzed. Since the luminescence of VO 4 3- and Pr 3+ has significantly different temperature-dependent behaviors, a new fluorescence intensity ratio thermometry strategy is realized. Temperatures range from 303-353 K, and the maximum absolute and relative sensitivities are 0.651 K -1 and 3.112% K -1 @ 353 K, respectively, much higher than the traditional thermally coupled level thermometry strategy. In addition, there is no obvious overlap between the emission peaks of VO 4 3- and Pr 3+ , which provides a good discrimination ability for signal detection. The above results show that this work provides a promising path to design self-reference optical thermometry materials with excellent temperature sensitivity and signal discrimination.
physics, multidisciplinary