The influence of thixotropy on the magnetorheological property of oil-based ferrofluid

Chuncheng Yang,Zhong Liu,Mengchun Yu,Xiufang Bian
DOI: https://doi.org/10.1016/j.molliq.2020.114425
IF: 6
2020-12-01
Journal of Molecular Liquids
Abstract:<p>A Fe<sub>3</sub>O<sub>4</sub> hydrocarbon oil-based ferrofluid was synthesized and its magnetorheological behavior was investigated. The ferrofluid exhibits shear thinning behavior under different magnetic fields and a significant hysteresis effect was observed from the viscosity-shear rate flow curves due to the thixotropy of ferrofluid. The thixotropic behavior is induced by the presence and evolution of the microstructures in the ferrofluid. Moreover, the experimental results demonstrate that the viscosity of the ferrofluid decreases with increasing magnetic field when the magnetic field is below 81 mT. This is followed by an abrupt increase in the viscosity when the magnetic field increases to 124 mT. However, the viscosity again decreases as the magnetic field continue to increase beyond 124 mT. We reveal the negative correlations between viscosity and magnetic fields. The unusual magnetorheological behavior of the ferrofluid is due to the joint effect of thixotropy and magnetic fields. These findings provide a new perspective on the rheological behaviors of ferrofluids that takes the thixotropic effect into consideration.</p>
chemistry, physical,physics, atomic, molecular & chemical
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to explore the magnetorheological properties of oil - based ferrofluid (FF) under different magnetic field intensities, especially the shear - thinning behavior and the hysteresis effect in magnetorheological properties. The study focuses on the influence of the thixotropy of ferrofluid on these properties. Specifically, the paper experimentally studies the magnetorheological behavior of Fe₃O₄ nanoparticles in hydrocarbon - oil - based ferrofluid, analyzes the variation law of ferrofluid viscosity under the combined action of thixotropy and magnetic field, and reveals the influence of the formation and evolution of microstructure in ferrofluid on magnetorheological behavior. ### Research Background - **Ferrofluid (FF)**: It is a material that responds to magnetic fields and has both the fluidity of a liquid and the magnetism of a solid. It is a stable colloidal suspension composed of nanoscale magnetic particles dispersed in water or an organic solvent and is widely used in engineering, medicine, and biology, etc. - **Magnetorheological Properties**: The rheological properties of ferrofluid can be significantly changed by applying a magnetic field, and this change is related to the formation and evolution of the microstructure inside the fluid. - **Thixotropy**: It refers to the phenomenon that the viscosity of a material decreases with time under the action of shear force, and when the shear force stops, the viscosity gradually recovers. This phenomenon is related to the formation and destruction of the microstructure inside the material. ### Research Methods - **Sample Preparation**: Fe₃O₄ nanoparticles were synthesized by the co - precipitation method and surface - modified with oleic acid to prepare a hydrocarbon - oil - based ferrofluid. - **Characterization Techniques**: X - ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM), dynamic light scattering (DLS), and thermogravimetric analysis (TGA) were used to characterize the structure, morphology, particle size distribution, and thermal stability of the nanoparticles. - **Magnetic Property Testing**: A vibrating sample magnetometer (VSM) was used to measure the hysteresis loops of the nanoparticles and ferrofluid. - **Rheological Property Testing**: A rotary rheometer (Anton Paar MCR 301) combined with a magnetorheological device (MRD170) was used to study the rheological properties of ferrofluid under different magnetic field intensities. ### Main Findings - **Shear - thinning Behavior**: Ferrofluid exhibits shear - thinning behavior under different magnetic field intensities, that is, the viscosity decreases as the shear rate increases. - **Hysteresis Effect in Magnetorheological Properties**: A significant hysteresis effect was observed in the viscosity - shear rate curve, which is caused by the formation and destruction of the microstructure inside the ferrofluid. - **Relationship between Viscosity and Magnetic Field**: At lower magnetic field intensities (< 81 mT), the viscosity of ferrofluid decreases as the magnetic field intensity increases; when the magnetic field intensity reaches 124 mT, the viscosity suddenly increases; when the magnetic field intensity continues to increase (> 124 mT), the viscosity decreases again. - **Influence of Thixotropy**: Thixotropy and the magnetic field act together, causing the magnetorheological behavior of ferrofluid to show a non - monotonic trend. At low magnetic field intensities, thixotropy plays a dominant role; at high magnetic field intensities, the magnetic field plays a dominant role. ### Conclusion This study reveals the complex mechanism of the magnetorheological behavior of ferrofluid under the combined action of thixotropy and magnetic field, providing a new perspective for understanding the rheological properties of ferrofluid. These findings are of great significance for the application of ferrofluid in the industrial and medical fields.