Abstract:Besides reducing pollution and removing urea from wastewater, electro-oxidation of urea has also offered new prospects for filling the overall water gap for economically producing hydrogen. In this regard, a simple and low-cost electrochemical deposition technique was used to prepare a highly efficient bifunctional electrocatalyst for the HER and the UOR (in place of the OER) on nickel foam (NiFeSP/NF). A three-dimensional and nanoporous NiFeSP/NF electrocatalyst demonstrated relatively high stability and electrocatalytic activity. Notably, the bimetallic and dual-anionic NiFeSP/NF electrode demonstrated good performance for the HER (42, 111 and 138 mV at current densities of −10, −100, and −200 mA cm −2 , respectively), the OER (1.451, 1.502, 1.528, and 1.576 V vs. RHE at 10, 100, 200 and 400 mA cm −2 , respectively), and the UOR (1.304, 1.346, 1.389 and 1.473 V vs. RHE at current densities of 10, 100, 200 and 400 mA cm −2 , respectively). Moreover, the use of a NiFeSP/NF||NiFeSP/NF pair as an anode and a cathode in an overall water-splitting system assisted by urea achieved 1.348 and 1.582 V vs. RHE at 10 and 100 mA cm −2 in 1.0 M KOH with 0.33 M urea solution, which are 163 and 234 mV lower than those achieved in 1.0 M KOH alkaline solution, respectively. Additionally, the NiFeSP/NF||NiFeSP/NF pair demonstrates long-term stability (30 h) in a chronopotentiometry test at 100 mA cm −2 in 1.0 M KOH with 0.33 M urea solution. This bimetallic and dual-anionic NiFeSP electrode exhibits substantial catalytic activity due to the appropriate synergy between Fe and Ni, the modification of the electronic structure enabled by the dual anions, and the enhanced electrocatalytically active surface caused by high porosity. The low cost and single-step manufacturing method of the NiFeSP electrode, high electrocatalytic activity, and stability make it potentially ideal for commercial use in hydrogen generation and treatment of wastewater containing urea.

Facile, Controllable, and Ultrathin NiFe-LDH In Situ Grown on a Ni Foam by Ultrasonic Self-Etching for Highly Efficient Urine Conversion

Anion Modulate the Morphological and Electronic Structure of NiFe-based Electrocatalyst for Efficient Urea Oxidation-Assisted Water Electrolysis

Synergistic Etching of Nickel Foam by Fe3+ and Cl− Ions to Synthesize Nickel-Iron-layered Double Hydroxide Nanolayers with Abundant Oxygen Vacancies for Superior Urea Oxidation

Amorphous iron-doped nickel boride with facilitated structural reconstruction and dual active sites for efficient urea electrooxidation

Electrochemically Induced Cu-NiOOH/Cu2O/Cu Mesh Heteroarchitecture with Cu-Ni Dual Active Sites As Efficient Bifunctional Electrocatalyst for Urea-Assisted Energy-Saving Hydrogen Production in Alkaline Electrolyte

Ni0-rich Ni/NiO Nanocrystals for Efficient Water-To‑hydrogen Conversion Via Urea Electro-Oxidation

Rapid Conversion of Co2+ to Co3+ by Introducing Oxygen Vacancies in Co3O4 Nanowire Anodes for Nitrogen Removal with Highly Efficient H2 Recovery in Urine Treatment.

Enhancing hydrogen generation through urea electro-oxidation on a bimetallic and dual-anionic NiFeSP/NF nanostructured electrode

Highly selective urea electrooxidation coupled with efficient hydrogen evolution

Ni‐Fe Layered Double Hydroxide Nanosheets Supported on Exfoliated Graphite for Efficient Urea Oxidation in Direct Urea Fuel Cells

Porous NiO Nanosheet Bifunctional Electrodes Modified with Ultrafine Ni3S2 Quantum Dots for Green Hydrogen Production Via Urea Electrolysis

Co-doped MnS/NiS/Ni3S2 in situ grown on hydrophilic nickel foam for energy-efficient urea-assisted alkaline hydrogen production

Built-in electrophilic/nucleophilic domain of nitrogen-doped carbon nanofiber-confined Ni2P/Ni3N nanoparticles for efficient urea-containing water-splitting reactions

PEO-PPO-PEO induced holey NiFe-LDH nanosheets on Ni foam for efficient overall water-splitting and urea electrolysis

Low-Cost Ni2P/Ni0.96S Heterostructured Bifunctional Electrocatalyst toward Highly Efficient Overall Urea-Water Electrolysis

Fe7Se8@Fe2O3 heterostructure nanosheets as bifunctional electrocatalyst for urea electrolysis

Coupling of NiFe Layered Double Hydroxides with Sulfides for Highly Efficient Urea Electrolysis and Hydrogen Evolution

Nickel Nanocrystals Anchored Nitrogen-Doped Carbon Derived from Eggshell Membrane as an Efficient Catalyst for the Electrocatalytic Oxidation of Urea

The In Situ Construction of NiFeS on Stainless Steel Mesh as an Efficient Electrocatalyst for UOR

Coaxial Ni-S@N-Doped Carbon Nanofibers Derived Hierarchical Electrodes for Efficient H2 Production Via Urea Electrolysis.

Electrocatalysis for Urea Evolution and Oxidation Through Confining Atomic Ni Into In2O3 Nanosheet Catalysts