ZnS-SnS@NC Heterostructure as Robust Lithiophilicity and Sulfiphilicity Mediator toward High-Rate and Long-Life Lithium–Sulfur Batteries
Weiqi Yao,Weizhong Zheng,Jie Xu,Chengxiang Tian,Kun Han,Weizhen Sun,Shengxiong Xiao
DOI: https://doi.org/10.1021/acsnano.1c00270
IF: 17.1
2021-03-25
ACS Nano
Abstract:Lithium–sulfur (Li–S) batteries are severely hindered by the low sulfur utilization and short cycling life, especially at high rates. One of the effective solutions to address these problems is to improve the sulfiphilicity of lithium polysulfides (LiPSs) and the lithiophilicity of the lithium anode. However, it is a great challenge to simultaneously optimize both aspects. Herein, by incorporating the merits of strong absorbability and high conductivity of SnS with good catalytic capability of ZnS, a ZnS-SnS heterojunction coated with a polydopamine-derived N-doped carbon shell (denoted as ) with uniform cubic morphology was obtained and compared with the ZnS-SnS<sub>2</sub>@NC heterostructure and its single-component counterparts ( and SnS<sub>2</sub>@NC). Theoretical calculations, <i>ex situ</i> XANES, and <i>in situ</i> Raman spectrum were utilized to elucidate rapid anchoring-diffusion-transformation of LiPSs, inhibition of the shuttling effect, and improvement of the sulfur electrochemistry of bimetal ZnS-SnS heterostructure at the molecular level. When applied as a modification layer coated on the separator, the cell with optimized lithiophilicity and sulfiphilicity enables desirable sulfur electrochemistry, including high reversibility of 1149 mAh g<sup>–1</sup> for 300 cycles at 0.2 C, high rate performance of 661 mAh g<sup>–1</sup> at 10 C, and long cycle life with a low fading rate of 0.0126% each cycle after 2000 cycles at 4 C. Furthermore, a favorable areal capacity of 8.27 mAh cm<sup>–2</sup> is maintained under high sulfur mass loading of 10.3 mg cm<sup>–2</sup>. This work furnishes a feasible scheme to the rational design of bimetal sulfides heterostructures and boosts the development of other electrochemical applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c00270?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c00270</a>.Additional experimental sections (materials synthesis, characterizations, and DFT calculations); SEM, TEM, XRD, TG, XPS, BET, and XANES characterizations of the samples; CV curves; discharge–charge profiles and cycle performance of various electrodes; <i>in situ</i> Raman tests; optimized geometries of LiPSs; Tables S1–S6: Li<sup>+</sup> diffusion rates, EIS fitting, and comparisons of electrochemical performance (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c00270/suppl_file/nn1c00270_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology