Abstract:Aiming at regulating building temperature in summer, the preparation and optimization of TiO 2 @n-octadecane microcapsules were studied in this paper, which is significant to energy conservation. N-octadecane and TiO 2 act as the core material and shell material, respectively. The SEM, FT-IR, DSC, TGA, and infrared thermal imaging were used to analyze the TiO 2 @n-octadecane microcapsules. Aiming at the enthalpy of phase transition and encapsulation rate of microcapsules, the reaction vessel, emulsifier, stirring rate, amount of acetic acid, and droplet-adding rate for preparing microcapsules were optimized. Furthermore, the microcapsules with the best properties were mixed into concrete to analyze their temperature regulation performance, mechanical strength, fire resistance, thermogravimetry, and cyclic stability. The effect of microcapsule proportions on the temperature regulation ability of concrete at different temperatures was also studied. The key findings are as follows: Firstly, the TiO 2 @n-octadecane microcapsules exhibit a stable core–shell structure and a size of about 1 μm. The highest melting enthalpy, crystallization enthalpy, and encapsulation rate of TiO 2 @n-octadecane microcapsules are 120 J/g, 116 J/g, and 54.1 %, respectively. The microcapsules only consist of TiO 2 and n-octadecane without any chemical reactions. Secondly, the concrete incorporating the TiO 2 @n-octadecane microcapsules shows a faster phase change reaction, inhibiting temperature rise or fall effectively, and preventing leakage. Thirdly, compared with ordinary concrete, 5 mm concrete with 20 % TiO 2 @n-octadecane microcapsules can extend its temperature below 28.5 °C for 15.7, 14.0, and 7.6 min at 30 °C, 35 °C, and 40 °C, respectively. Finally, the compressive strength of concrete with 0 %∼20 % MPCMs satisfies the requirements for concrete applications. It also has excellent fire resistance and thermal stability. Moreover, incorporating MPCMs into concrete can significantly reduce the pyrolysis of MPCMs.

Study on the preparation and properties of TiO 2 @n-octadecane phase change microcapsules for regulating building temperature

Preparation and Characterization of Fatty Acid Ternary Eutectic Mixture/Nano-Sio 2 Composite Phase Change Material for Building Applications

Titanyl sulfate-based TiO 2 -paraffin phase change microcapsules: Evaluation of alkyltriethoxysilane modification and thermoregulation applications

Preparation and Properties of Thermal Energy Storage and Temperature Regulation Microcapsulated Paraffin by P(MMA-co-AA)

Preparation and thermal properties of nano-microcapsule and simulation heat storage application

Phase change n-Octadecane microencapsulated in titanium dioxide nanoparticle-doped polymer for photothermal conversion and photocatalysis

Fabrication and Properties of Microencapsulated N-Octadecane with TiO2 Shell As Thermal Energy Storage Materials

Preparation and Characterization of Microencapsulated Phase Change Materials for Solar Heat Collection

A novel measurement method of thermal performances for an improved thermal storage concrete with microencapsulated phase change materials

Microencapsulated phase change materials with TiO2-doped PMMA shell for thermal energy storage and UV-shielding

Preparation and Characterization of Phase Change Material Microcapsules with Carbon Nanotubes Loaded with MgAl Layered Double Hydroxides for Controlling Temperature in the Building

Microencapsulated phase change n-Octadecane with high heat storage for application in building energy conservation

Preparation and Characterization of Poly (Mma-Co-aa)/paraffin Microencapsulated Phase Change Material for Thermal Energy Storage

Thermal characterization and analysis of n-octadecane microcapsules modified with MnO2 particles

Synthesis and Characterization of Microencapsulated Paraffin with Titanium Dioxide Shell As Shape-Stabilized Thermal Energy Storage Materials in Buildings

Synthesis and Properties of Microencapsulated Octadecane with Silica Shell As Shape–stabilized Thermal Energy Storage Materials

Fabrication and properties analysis of paraffin@TiO2/Ag phase change microcapsules for thermal energy storage and photocatalysis

Optimal Integration of Phase-Change Microcapsules and Nano-Silica for Improving the Strength of Phase-Change Concrete

Microencapsulated N-Octadecane with Different Methylmethacrylate-Based Copolymer Shells As Phase Change Materials for Thermal Energy Storage

Preparation and characterization of microencapsulated n -octadecane as phase change material with different n -butyl methacrylate-based copolymer shells

Synthesis of phase change microcapsules with binary fatty acid ester core and their feasibility investigation in energy conservation of cementitious materials