Abstract:Y2O3-Al2O3-SiO2 (Y-Al-Si-O, YAS) glass is a highly promising material offering resistance against calcium magnesium aluminosilicate (Ca-Mg-Al-Si-O, CMAS) corrosion, and it is an excellent candidate for environmental barrier coating (EBC). In this study, influence of composition on YAS glass properties and CMAS corrosion resistance at 1300 degrees C was investigated, and the result indicated that most sets of YAS glass possessed the superior CMAS resistance than yttrium disilicate. The increase of Y2O3 content and decrease of Al/Si ratio both resulted in a higher nucleation rate during heating. Moreover, when YAS was subjected to the molten CMAS corrosion, two types of corrosion restraining behaviors were observed. One is the generation of anorthite layer on YAS with high-optical basicity, and the recession depth becomes less than that of yttrium disilicate. Stacking of anorthite grains obstructs the diffusion of Y to the corrosion front, which inhibits the corrosion. The other mechanism involves the generation of calcium yttrium cyclosilicate layer at similar to 1270 degrees C first on YAS with low-optical basicity. Next, with the increase in the temperature, the reaction changes to generate an amorphous phase. Moreover, the layer acts as a barrier to restrain the corrosion. Furthermore, the difference between the two corrosion behaviors was explained based on the optical basicity (OB) theory calculation, and a YAS composition region with excellent resistance toward CMAS corrosion was predicted. The region with an OB higher than that of CMAS shows superior CMAS resistance, in particular, for the portion with a lower difference in values of OB between the two substances.

Thermal corrosion behavior of Yb4Hf3O12 ceramics exposed to calcium-ferrum-alumina-silicate (CFAS) at 1400 °C

Interaction and infiltration behavior between Calcium‐Ferrum‐Alumina‐Silicate and Yb4Hf3O12 ceramics at various temperatures

Corrosion behavior of Yb4Hf3O12 ceramics exposed to Calcium-Ferrum-Alumina-Silicate (CFAS) coupled with water vapor at 1400 °C

Interaction of Yb2Si2O7 environmental barrier coating material with Calcium-Ferrum-Alumina-Silicate (CFAS) at high temperature

Calcium‐ferrum‐alumina‐silicate (CFAS) corrosion behavior of Lu4Hf3O12 ceramics at 1400°C

Corrosion behavior and mechanism of ytterbium monosilicate by molten calcium-magnesium-alumino-silicate melts at 1400 °C and 1500 °C

Interaction of ytterbium monosilicate environmental barrier coating material with molten calcium-magnesium-aluminosilicate (CMAS)

Corrosion behavior of ytterbium hafnate exposed to water-vapor with Al(OH) 3 impurities

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics

Effect of CaF2 on sintering behavior and thermal shock resistance of Y2O3 materials

Thermal aging and CMAS corrosion behaviors of Y2SiO5 ceramic for environmental barrier coatings

Outstanding molten calcium–magnesium–aluminosilicate (CMAS) corrosion resistance of directionally solidified Al2O3/Y3Al5O12 eutectic ceramic at 1500°C

Properties evaluation and failure behaviour of plasma sprayed Y4Hf3O12 for thermal barrier coating applications

High temperature corrosion behavior and the inhibition of apatite formation evolving from corrosion of (Y1−Yb )2SiO5 in water vapor environment

Interaction between Y-Al-Si-O glass-ceramics for environmental barrier coating materials and Ca-Mg-Al-Si-O melts

CMAS Corrosion Behavior of Mid-Entropy Rare-Earth Hafnate (Y0.3Gd0.3Yb0.4)4Hf3O12 as Thermal Barrier Coating Candidate

Plasma sprayed Yb4Hf3O12 thermal barrier coatings with excellent thermophysical properties and robust CMAS corrosion resistance

Growth kinetics of apatite layer evolved from calcia-magnesia-aluminosilicate (CMAS) hot corrosion reaction of (Y1-Yb )2SiO5 ceramics at elevated temperatures of 1673 K and 1773 K

High-temperature Corrosion of the Gd4Al2O9 Ceramics Exposed to Calcium–magnesium–aluminum-Silicate Melts

Initial corrosion mechanism of Hf6Ta2O17 ceramic for TBCs against CMAS infiltration: Experiment and first-principle simulation

Corrosion behavior and mechanism of ytterbium silicates environmental barrier coatings to thermal cycling in water vapor