Large-Scale Fabrication of Form-Stable Phase Change Nanotube Composite for Photothermal/Electrothermal Energy Conversion and Storage
Lingbo Kong,Zhiyuan Wang,Xiangfei Kong,Lu Wang,Zhiyong Ji,Xiaomei Wang,Xu Zhang
DOI: https://doi.org/10.1021/acsami.1c07160
2021-06-17
Abstract:Photothermal/electrothermal advanced functional form-stable phase change materials (FSPCMs) can efficiently make use of solar energy and electrical energy by using supporting materials to encapsulate phase change materials. Herein, a novel low-cost integrated supporting material, denoted PDVB-12/PPy NTs, is quickly constructed via wrapping the polypyrrole (PPy) on the mesoporous polydivinylbenzene nanotubes (PDVB-12 NTs) through a fast oxidative initiation method. PDVB-12/PPy NTs exhibits good loading capacity (72.9 wt %) for industrial paraffin wax (IPW) due to the large specific surface area, and the resulting FSPCM composite (/PPy) exhibits a large latent heat of fusion (145.7 J/g), high thermal stability, and excellent shape stability. In addition, PPy imparts the /PPy composite with high electrical conductivity (55.6 S m<sup>–1</sup>) and high photoabsorption ability (whole visible light band). The energy stored in the /PPy composite could be triggered and released under relatively low voltages (2.5 V) with electrothermal energy conversion efficiency (89.6%) or solar radiation (100 mW cm<sup>–2</sup>) with photothermal energy conversion efficiency (85.2%). This study provides a low-cost and fast method for large-scale fabrication of supporting materials, which can be a good candidate in energy storage applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c07160?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c07160</a>.FT-IR spectra of PDVB NTs, PDVB-12 NTs, PDVB-12/PPy NTs, IPW, and /PPy; XRD patterns of IPW and /PPy; TGA analysis of IPW, PDVB-IPW, PDVB-12-IPW, and /PPy; SEM images of /PPy composite; DSC curves of IPW-20 and /PPy, IPW-30 and /PPy, IPW-50 and /PPy; SEM images of /PPy, /PPy, and /PPy; digital pictures of leaking test of /PPy, /PPy, and /PPy; IR images of IPW and /PPy under light irradiation of 100 mW/cm<sup>2</sup>; photograph and IR images of /PPy at 2.2 V; electrical current evolution curves passing through PDVB-12/PPy NTs at a voltage of 1.5–2.5 V and temperature variation curves of PDVB-12/PPy NTs at 1.5–2.5 V; structural parameters and IPW loadings of the PDVB NTs at different F–C reaction timse; phase change characteristics of IPW, PDVB-12-IPW, and /PPy; phase change characteristics of IPW-20, IPW-30, IPW-50, /PPy, /PPy, and /PPy (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c07160/suppl_file/am1c07160_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology