Abstract:Flexible asymmetric supercapacitor (FASC) systems are expected to exhibit not only excellent energy storage properties and safety but also satisfactory flexibility and robust integration. However, tremendous issues such as low capacitance, narrow voltage window, and poor mechanical properties still exist. In this paper, a novel kind of 3D lamellar Mn(OH)2 nanosheets on Cu-plated carbon cloth with a core-shell integrated framework (@Mn(OH)2) is fabricated to obtain the flexible material in the FASC. In this unique @Mn(OH)2 electrode material, the high theoretical specific capacity of CuO and Mn(OH)2 brings superior energy storage properties. Meanwhile, as the shell part, the deposited Mn(OH)2 layer and coated CuO layer work as both capacity contributors and substrate protectors, simultaneously maintaining the high capacitance and satisfactory flexibility of the electrodes. Therefore, the capacitance successfully achieves around 8140 mF cm–2 under 0.5 mA cm–2. Significantly, the assembled FASC (named as @Mn(OH)2//) achieves a working voltage of up to 2.4 V. In the case of a high-power density close to 34.31 mW cm–3, its energy density reaches around 6.29 mW h cm–3. Moreover, the capacity holds 88.9% even after 10,000 cycles, showing its great application potential in the field of wearable electronics.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acssuschemeng.1c05164.Supplementary data chart of @Mn(OH)2 electrode material characterization and morphology images, optimal exploration of the Mn(OH)2 deposition time and deposition voltage, and practical characterization of assembled flexible supercapacitor devices (PDF)This article has not yet been cited by other publications.

Construction of flexible MnCo 2 O 4 @FeCoNi-LDH electrode materials with nanoflower-like and hierarchical structure for high-performance asymmetric supercapacitor

Constructing nickel cobaltate @nickel-manganese layered double hydroxide hybrid composite on carbon cloth for high-performance flexible supercapacitors

Hierarchical FeCo2O4@NiCo Layered Double Hydroxide Core/shell Nanowires for High Performance Flexible All-Solid-state Asymmetric Supercapacitors

Porous NiCo2O4–FeCo2O4 Nanowire Arrays As Advanced Electrodes for High-Performance Flexible Asymmetric Supercapacitors

Construction of hierarchical FeCo2O4@MnO2 core-shell nanostructures on carbon fibers for high-performance asymmetric supercapacitor

MXene-MnO2-CoNi layered double hydroxides//activated carbon flexible asymmetric supercapacitor

NiMn2O4/CoS Nanostructure Electrode Material for Flexible Asymmetric Supercapacitors

A Flexible All-Solid-state Asymmetric Supercapacitors Based on Hierarchical Carbon Cloth@comoo4@nico Layered Double Hydroxide Core-Shell Heterostructures

In Situ Growth of 3D Lamellar Mn(OH) 2 on CuO-Coated Carbon Cloth for Flexible Asymmetric Supercapacitors with a High Working Voltage of 2.4 V

Three-dimensional hierarchical core-shell CuCo2O4@Co(OH)2 nanoflakes as high-performance electrode materials for flexible supercapacitors

Hierarchical graphene oxide/manganese dioxide/cobalt-nickel layered double hydroxide electrodes for high energy density asymmetric flexible supercapacitor

CoNi2S4 Nanosheets on Nitrogen-Doped Carbon Foam As Binder-Free and Flexible Electrodes for High-Performance Asymmetric Supercapacitors

Oxygen vacancies enhancing hierarchical NiCo2S4@MnO2 electrode for flexible asymmetric supercapacitors

Hierarchical MnCo2O4@CuCo2O4 Core-Shell Nanoarrays on Carbon Cloth As Binder-Free Electrode for Flexible All-Solid-state Asymmetry Supercapacitors

High performance flexible asymmetric supercapacitor constructed by cobalt aluminum layered double hydroxide @ nickel cobalt layered double hydroxide heterostructure grown in-situ on carbon cloth

Facile Synthesis of Free-Standing NiO/MnO 2 Core-Shell Nanoflakes on Carbon Cloth for Flexible Supercapacitors

Constructing a 3D multichannel structure to enhance performance of Ni–Co–Mn hydroxide electrodes for flexible supercapacitors

Electrochemically Synthesis of Nickel Cobalt Sulfide for High-Performance Flexible Asymmetric Supercapacitors.

Metal-organic Framework Derived Hierarchical NiCo2O4 Triangle Nanosheet Arrays@sic Nanowires Network/carbon Cloth for Flexible Hybrid Supercapacitors

Hierarchical layered nickel-iron double hydroxide/carbon nanotube fiber electrode for constructing asymmetric fiber supercapacitor

Constructing metal organic framework derived manganese cobalt layered double hydroxide nanosheets on Ni foam as cost-effective binder-free electrodes of high-performance supercapacitors