High Consistency Silicone Rubber Foams

Timo Hofmann,Ralf-Urs Giesen,Hans-Peter Heim

DOI: https://doi.org/10.3390/polym16091181

IF: 5

2024-04-24

Polymers

Abstract:Silicone elastomers are high-performance plastics. In the extrusion process, only high-consistency silicone rubbers were used. In order to reduce the cost and weight, silicone rubbers can be foamed during processing. In this study, high-consistency silicone rubber is processed with different physical and chemical blowing agents. The resulting reaction kinetics, as well as the mechanical and morphological properties, had been investigated and compared with each other. This showed that the chemical blowing agent significantly influenced the crosslinking reaction compared to the microspheres and the water/silica mixture tested, but it also achieved the lowest density compared to the physical blowing agents. When evaluating the foam morphology, it became clear that the largest number of pores was achieved with the microspheres and the largest pores when using the water/silica mixture. Furthermore, it has been shown that the different mechanisms of action of the blowing agents have a major influence on the mechanical properties, such as the micro shore hardness and the foam morphology.

polymer science

What problem does this paper attempt to address?

### What problem does this paper attempt to solve?

This paper primarily explores the performance and influencing factors of high-consistency silicone rubber (HCR) during the foaming process. Specifically:

1. **Selection and Comparison of Foaming Agents**:
- The study investigates the effects of different types of foaming agents on the foaming performance of silicone rubber, including chemical foaming agents (such as azodicarbonamide (AZDN)) and physical foaming agents (such as thermoplastic microspheres and water/silica mixtures).
- It compares the impact of these foaming agents on the crosslinking reaction, mechanical properties, and foam morphology of silicone rubber.

2. **Crosslinking Reaction During the Foaming Process**:
- The study examines the influence of different foaming agents on the crosslinking behavior of silicone rubber, particularly the changes in the torque curve during the crosslinking process.
- Chemical foaming agents significantly affect the speed and extent of the crosslinking reaction, while the impact of physical foaming agents is relatively minor.

3. **Foam Density and Hardness**:
- The density of silicone rubber foam treated with different foaming agents was measured, revealing that chemical foaming agents can achieve the lowest density (approximately 0.4 g/cm³), while microspheres among the physical foaming agents showed a relatively low density (approximately 0.48 g/cm³).
- In terms of hardness, samples treated with chemical foaming agents exhibited lower hardness (5-8 micro shore A), whereas samples treated with physical foaming agents (microspheres) showed higher hardness (20-23 micro shore A).

Through these studies, the paper aims to find a foaming method that can effectively reduce the density of silicone rubber while maintaining good mechanical properties, thereby achieving material lightweighting and cost optimization.