Abstract:Nanostructures of Ti3C2Tx, one of the members of the MXenes family, have been successfully prepared by chemical etching of Al from Ti3AlC2 (MAX phase) using Hydrofluoric Acid (HF) for various etching durations at room temperature. The phase, morphological, structural, and chemical analysis was performed using XRD, FESEM, TEM, Raman, and X-Ray photoelectron spectroscopy. The surface morphology of as-synthesized Ti3C2Tx (MXene) phase is characterized by stacked of layered sheets like structures. Field electron emission (FEE) was investigated at base pressure of 1 x 10-8 mbar. The pristine Ti3AlC2 (MAX) and Ti3C2Tx (MXene) nanosheets emitters showed values of turn-on field (defined at current density ~ 1 μA/cm2) as 4.18 and 1.67 V/μm, respectively. Furthermore, maximum emission current density of ~ 825 μA/cm2 was extracted from the MXene nanosheets emitter at an applied field of 3.60 V/μm, in contrast to ̴ 71 μA/cm2 drawn at 7.31 V/μm from the pristine MAX emitter. The MXene nanosheets emitter exhibited good emission current stabilities at pre-set values ~ 10 and 100 μA over 3 hours duration. Work function values of the MAX and MXene nanosheets emitters were measured using a retarding field analyzer, and found to be 4.4 and 3.6 eV, respectively. Extensive ab-initio simulations have been performed to provide structural and electronic properties, as well as for estimating the work function of Ti3C2 layered material. The estimated electronic density of states revealed its metallic character. The improved FEE performance exhibited by the 2D layered Ti3C2Tx (MXene) nanosheets emitter is attributed to its unique morphology characterized by high aspect ratio, metallic electronic properties and relatively lower work function.

Piezoelectricity in Monolayer and Multilayer Ti 3 C 2 Tx MXenes: Implications for Piezoelectric Devices

Piezoelectricity in monolayer MXene for nanogenerators and piezotronics

Piezoelectric behavior of single-layer oxidized-MXene for nanogenerators and piezotronics

Large Out-of-plane Piezoelectricity of Oxygen Functionalized MXenes for Ultrathin Piezoelectric Cantilevers and Diaphragms

Theoretical study of piezoelectric and light absorption properties, and carrier mobilities of Janus TiPX (X = F, Cl, and Br) monolayers

Tuning the Electrical Conductivity of Ti2CO2 MXene by Varying the Layer Thickness and Applying Strains

Broadband High-Performance Microwave Absorption of the Single-Layer Ti3C2Tx MXene

Synthesis, physico-chemical characterization, DFT simulation, and field electron behaviour of 2D layered Ti3C2Tx MXene nanosheets

Atomic-scale recognition of surface structure and intercalation mechanism of Ti3C2X.

Mechanical Elasticity and Piezoelectricity in Monolayer Transition-Metal Dichalcogenide Alloys

Two-dimensional Ti3C2 MXene-based Nanostructures for Emerging Optoelectronic Applications

Charge Carriers Localization Effect Revealed through Terahertz Spectroscopy of MXene: Ti3C2Tx

Facile Fabrication and High Field Emission Performance of 2-D Ti<sub>3</sub>C<sub>2</sub>T<i><sub>x</sub></i> MXene Nanosheets for Vacuum Electronic Devices

Signatures of Band-like Optical and Charge Transport in Ti3C2Tx MXene Flakes

High-performance piezoelectric composites via β phase programming

Two-dimensional Janus MXTe (M = Hf, Zr; X = S, Se) piezoelectrocatalysts: A comprehensive investigation of itselectronic, synthesis feasibility, electric polarization, and hydrogen evolution reaction activity

Dependence of Elastic and Optical Properties on Surface Terminated Groups in Two-Dimensional MXene Monolayers: a First-Principles Study

Atomic Defects in Monolayer Titanium Carbide (Ti3C2Tx) MXene

Nanoscale Surface and Bulk Electronic Properties of Ti3C2Tx MXene Unraveled by Multimodal X‐Ray Spectromicroscopy

Coexistence of large out-of-plane and in-plane piezoelectricity in 2D monolayer Li-based ternary chalcogenides LiMX2

Surface termination dependence of electronic and optical properties in Ti$_2$CO$_2$ MXene monolayers