Phenediamine bridging phthalocyanine-based covalent organic framework polymers as anode materials for lithium-ion batteries
Luyi Wang,Jianjun Zhao,Jun Chen,Tingting Jiang,Qian Zhang,Shengwen Zhong,Dmytro Sydorov
DOI: https://doi.org/10.1039/d3cp00007a
IF: 3.3
2023-02-18
Physical Chemistry Chemical Physics
Abstract:In this work, phenediamine bridging phthalocyanine-based covalent organic framework materials (CoTAPc-PDA, CoTAPc-BDA and CoTAPc-TDA) with increasingly-widening pore sizes are prepared by reacting cobalt octacarboxylate phthalocyanine with p-Phenylenediamine (PDA), Benzidine (BDA) and 4,4''-Diamino-p-terphenyl (TDA), respectively. The effects of frame size on the morphology structure and its electrochemical properties were explored. X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET) and Transmission electron microscopy (TEM) images show that the pore sizes of the CoTAPc-PDA, CoTAPc-BDA and CoTAPc-TDA are about 1.7 nm, 2.0 nm and 2.3 nm, respectively, which are close to the simulated results after the geometric conformation optimization by Material Studio software. In addition, the specific surface areas of CoTAPc-PDA, CoTAPc-BDA and CoTAPc-TDA are 62, 81 and 137 m2 g-1. With the increase of the frame size, the specific surface area of the corresponding material is also increasing, which is bound to produce different electrochemical behaviors. As a result, the initial capacities of the CoTAPc-PDA, CoTAPc-BDA and CoTAPc-TDA electrodes in lithium-ion batteries (LIBs) are 204, 251 and 382 mAh/g sequentially. As the charge and discharge process continues, the active points in the electrode material are continuously activated, leading to the continuous increase of the charge and discharge capacity. After 300th cycles, the CoTAPc-PDA, CoTAPc-BDA and CoTAPc-TDA electrodes presenting capacities of 519, 680 and 826 mAh g-1 respectively, and after 600 cycles, the capacities are maintained at 602, 701 and 865 mAh g-1, with a stable capacity retention rate at a current density of 100 mA g-1. The results show that the large-size frame structure materials have larger specific surface area and more favorable lithium ion transmission channels, producing greater active point utilization and smaller charge transmission impedance, thus showing larger charge and discharge capacity and more superior rate capability. This work fully confirms that frame size is a key factor affecting the properties of organic frame electrodes, providing design ideas for the development of high-performance organic frame electrode materials.
chemistry, physical,physics, atomic, molecular & chemical