Numerical simulation of melt flow and temperature field during DC casting 2024 aluminium alloy under different casting conditions

DOI: https://doi.org/10.1007/s41230-024-3099-5

2024-06-01

China Foundry

Abstract:Casting speed, casting temperature and secondary cooling water flow rate are the main process parameters affecting the DC casting process. These parameters significantly influence the flow and temperature fields during casting, which are crucial for the quality of the ingot and can determine the success or failure of the casting operation. Numerical simulation, with the advantages of low cost, rapid execution, and visualized results, is an important method to study and optimize the DC casting process. In the present work, a simulation model of DC casting 2024 aluminum alloy was established, and the reliability of the model was verified. Then, the influence of casting parameters on flow field and temperature field was studied in detail by numerical simulation method. Results show that with the increase of casting speed, the melt flow becomes faster, the depths of slurry zone and mushy zone increase, and the variation of slurry zone depth is greater than that of mushy zone. With an increase in casting temperature, the melt flow rate increases, the depth of the slurry zone becomes shallower, and the depth of the mushy zone experiences only minor changes. The simulation results further indicate that the increase of the flow rate of the secondary cooling water slightly reduces the depths of both slurry and mushy zone.

metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper primarily investigates the effects of casting speed, casting temperature, and secondary cooling water flow rate on the melt flow field and temperature field during the DC casting process of 2024 aluminum alloy. Specifically:

1. **Effect of Casting Speed**:
- Increasing the casting speed leads to a faster melt flow rate, and the depth of the slurry zone and mushy zone increases.
- When the casting speed increases from 25 mm/min to 76 mm/min, the flow rate of the melt at the hot top entrance increases from 8 mm/s to 20 mm/s, and the flow rate near the dam increases from 5 mm/s to 8 mm/s.
- The depth of the slurry zone increases from 9 mm to 133 mm, and the depth of the mushy zone increases from 56 mm to 84 mm.

2. **Effect of Casting Temperature**:
- An increase in casting temperature enhances the melt flow, deepens the sump, thins the slurry zone, while the mushy zone remains almost unchanged.
- When the casting temperature increases from 660 °C to 733 °C, the melt flow rate near the graphite ring increases from 1.9 mm/s to 9.6 mm/s; the depth from the liquid surface to the liquidus isotherm plus the slurry zone increases from 296 mm to 300 mm, and the depth of the slurry zone decreases from 82 mm to 63 mm.

3. **Effect of Secondary Cooling Water Flow Rate**:
- An increase in cooling water flow rate slightly reduces the depth of the slurry zone and mushy zone.
- When the cooling water flow rate increases from 230 L/min to 550 L/min, the depth of the mushy zone decreases from 62 mm to 60 mm, and the depth of the slurry zone decreases from 65 mm to 63 mm.

Through these studies, the paper aims to optimize casting process parameters to improve casting quality and production efficiency.